Investigation of the influence of VO2 formation on the structural morphology and magnetic properties in hydrothermally synthesized V6O13

Li Liu,Wei Zhu,Siyu Li,Qifu Bao,Tiangui Zhao,Detai Shi,Xiaolong Li,Jianer Zhou

DOI: https://doi.org/10.1007/s10854-024-12259-3

2024-03-05

Journal of Materials Science Materials in Electronics

Abstract:Investigating the impact of hydrothermal duration on electronic magnetism, two distinct samples were synthesized: the V 6 O 13 phase (S1) with 0.5 h of hydrothermal reaction, and the V 6 O 13 and VO 2 coexistent phase (S2) with 6 h of reaction. X-ray diffraction identified S1 as monoclinic C2/m, and S2 with a 4:1 ratio of V 6 O 13 in P21/c space group VO 2 . Electron microscopy revealed rod-like V 6 O 13 and spherical VO 2 . Both samples exhibited metal-insulator transitions, with the presence of VO 2 in S2 elevating the metal-insulator phase transition onset temperature and widening the transition range. S1 exhibits antiferromagnetic ordering at low temperatures (T N ~ 55 K) and follows the Curie-Weiss law above the metal-insulator transition temperature, while the behavior of S2 was modeled by a combination of Pauli and Curie-like paramagnetism, aligning well with experimental data. Small hysteresis loops in both samples suggested weak ferromagnetism; the linear loop of S1 indicated strong vanadium electron correlation, and the incomplete S-loop of S2 was attributed to the influence of VO 2 on the electronic magnetism of V 6 O 13 .

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied