High-performance Alnico magnets prepared by powder bed fusion
Zhi-Ying Zhang,Mu-Jing Zhou,Ji-Bing Sun,Bo Li,Shun Wang,Zhan Wang,Shu Wang,Zheng-Yan Zhang,Ying Zhang
DOI: https://doi.org/10.1016/j.jallcom.2023.173380
IF: 6.2
2024-01-04
Journal of Alloys and Compounds
Abstract:Fine-grained and anisotropic Alnico magnets were prepared by powder bed fusion using a laser beam. The as-built magnets were treated by solution treatment (ST) at 1250 °C, magnetic heat treatment (MHT) at 835 °C, and three-stage aging treatment (TSA) at 600 − 500 °C, respectively. The phase transition, microstructure evolution, and magnetic characteristics of the magnets were investigated. The findings demonstrate that as-built magnets are composed of equiaxed grains with a fine grain size of ∼1.5 μm and exhibit crystalline and magnetic anisotropy. After ST-MHT-TSA treatment, the magnets are composed of equiaxed grains with an average grain size of 12.1 − 15.5 μm, and every grain exhibits a spinodal structure consisting of the FeCo-type α 1 phase and the Fe 2 NiAl-type α 2 phase as well as enhanced orientation. The orientation relation between α 1 and α 2 mainly forms { 1 10}α 1 //{220}α 2 , {200}α 1 //{400}α 2 , and the atoms at the interface have a strong coherent matching. The spinodal structure in ST-MHT-TSA magnets mainly displays checkerboard-like. Both α 1 and α 2 phases exhibit a single domain structure; their interface is the magnetic domain wall. High α 1 aspect ratio and anisotropy give Alnico magnet exceptional magnetic performance with Hc= 1363.1 Oe, Br= 9.0 kGs, and (BH) max = 6.2 MGOe. Furthermore, micro-magnetic simulations were used to disclose how some defect structures in the micro-regions affect the magnetic properties.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering