Abstract:Eugenol-based epoxy resins have been extensively studied, but eugenol-derived curing agents have been less addressed. A curing agent is decisive to fundamental curing mechanisms and greatly affects intrinsic properties of finalized epoxy thermosets. Herein, we synthesize linear (2SiEU) and cyclic (4SiEU) siloxane-functionalized eugenol hardeners to cross-link multifunctional epoxy novolacs of bisphenol A (BNE200) and o-cresol (CNE202). How the linear and cyclic siloxane topologies of 2SiEU and 4SiEU affect the thermal, mechanical, fracture mechanical, and thermomechanical properties, water absorption, and wettability of resultant thermosets is highlighted. 4SiEU endows 4SiEU/BNE200 and 4SiEU/CNE202 thermosets with an elevated glass transition temperature from 52.9 and 53.9 °C to 97.3 and 89.4 °C (DSC), an increased residue (750 °C/N2) from 18.9 and 20.3% to 32.6 and 43.5%, an enhanced tensile strength from 48.1 and 46.8 MPa to 61.8 and 63.9 MPa, and an impact strength from 1.56 and 1.57 kJ·m–2 to 2.70 and 2.22 kJ·m–2, whereas the critical stress intensity factor (K IC) decreases from 1.56 and 1.67 MPa·m1/2 to 1.26 and 1.29 MPa·m1/2, respectively, compared to 2SiEU/BNE200 and 2SiEU/CNE202. All of the thermosets display the high tensile elongation at break, flexural strength, and flexural modulus above 7.3%, 72 MPa, and 2.1 GPa, respectively, with low water absorption (<∼1.8%). In general, the 4SiEU-incorporated cyclic siloxane moieties endow the superior overall performances to the obtained thermosets compared to 2SiEU because they function as additional cross-linkers and increase the content of thermally stable Si–O bonds, and they cause an additional secondary relaxation at a subroom temperature range. Nevertheless, 2SiEU delivers better fracture mechanical properties, which are likely more sensitive to the increased plastic deformation of the resin matrix. Altogether, 2SiEU and 4SiEU are capable of effectively cross-linking the standard epoxy novolacs exhibiting multiple properties of interest, expressing a good promise as robust hardeners for biobased epoxy thermosets.

Robust Vanillin-Derived Poly(thioether imidazoles) as Both a Latent Curing and Toughening Agent for One-Component Epoxy Resins

A robust fully bio-based aromatic-aliphatic ketone epoxide monomer for high-performance epoxy resin containing imine structural moiety

High-Performance One-Component Epoxy Adhesive Based on the Synergistic Effect of Lignin-Derived Triaryl-Imidazole and Phytic Acid

Imidazole substituted benzothiadiazole derivatives as latent curing agent for epoxy thermosetting resin

Amino acids as latent curing agents and their application in fully bio-based epoxy resins

Synthesis of a novel lignin‐based epoxy resin curing agent and study of cure kinetics, thermal, and mechanical properties

Facile synthesis of bio-based latent curing agent and its high-Tg epoxy network

Build-To-Specification Vanillin and Phloroglucinol Derived Biobased Epoxy-Amine Vitrimers

Design and Synthesis of Thiol-Terminated Imidothioether Oligomer As Thermally Latent Hardener and Modifier for High-Performance Epoxy/thiol Thermosets

Study on Vanillin Triggered Degradable Epoxy Via Facile One-Pot Synthesis

Impact Of Lignin Source On The Performance Of Thermoset Resins

Photocurable, Thermally Reprocessable, and Chemically Recyclable Vanillin-Based Imine Thermosets

Rigid-and-Flexible, Degradable, Fully Biobased Thermosets from Lignin and Soybean Oil: Synthesis and Properties

One-Pot Preparation of Double-Network Epoxy Vitrimers with High Performance, Recyclability, and Two-Stage Stress Relaxation

All‐In‐One Epoxy/MXene Nanocomposites with Bead‐Type Polymeric Imidazole Latent Curing Agent for Enhancing Storage Stability and Flame Retardancy

Effect of Synthetic Low-Odor Thiol-Based Hardeners Containing Hydroxyl and Methyl Groups on the Curing Behavior, Thermal, and Mechanical Properties of Epoxy Resins

Robustly Curing Epoxy Novolacs by Linear and Cyclic Siloxane-Functionalized Eugenol: Impact of Topologies of Cross-Linkers on Properties of Thermosets

Mechanically robust, hydrothermal aging resistant, imine-containing epoxy thermoset for recyclable carbon fiber reinforced composites

Optimal processing conditions of a bio-based epoxy synthesized from vanillyl alcohol

Fully rosin-based epoxy vitrimers with high mechanical and thermostability properties, thermo-healing and closed-loop recycling

Sustainable Epoxy Vitrimers from Epoxidized Soybean Oil and Vanillin