Three-dimensional graphene-wrapped Co0.85Se@C as high volumetric capacity anode material for lithium-ion batteries

Wen Ding,Xiaozhong Wu,Yanyan Li,Shuo Wang,Zhichao Miao,Pengfei Zhou,Jin Zhou,Shuping Zhuo

DOI: https://doi.org/10.1016/j.apsusc.2020.147746

IF: 6.7

2021-01-01

Applied Surface Science

Abstract:<p>To overcome the drawbacks of poor long-term cyclic and large volume expansion for selenides, which have high theoretical specific capacity and are promising candidates to fulfill the requirement of high volumetric energy density for lithium-ion batteries, we prepared a novel three-dimensional graphene-wrapped Co_0.85 composite (_0.85) through a capillary evaporation-induced drying method. This process leads to a shrinkage of graphene assembly, generating an ideal configuration compact composite material. XPS analysis confirms that the C-O-Co is formed from reactions between the Co_0.85 and oxygen-containing groups on graphene oxide during the preparation process. Such a strong covalent interaction between the Co_0.85 and graphene, together with its compact structure are favorable to high volumetric capacity. The electrochemical measurements show that the specific capacity of the GCS is about 1022.5 mAh g⁻¹ after 200 cycles at 0.1 A g⁻¹, corresponding to a remarkably reversible volumetric capacity of 2096.1 mAh cm⁻³. Moreover, good long-cycling durability and rate performance are also achieved. Consequently, this composite is a promising electrode material with high volumetric capacity in lithium-ion batteries.</p>

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films