Preparation of Fe 3 O 4 @PMAA@Ni Microspheres towards the Efficient and Selective Enrichment of Histidine-Rich Proteins

Yang Wang,Yingying Wei,Pengcheng Gao,Si Sun,Qian Du,Zhifei Wang,Yong Jiang

DOI: https://doi.org/10.1021/acsami.0c19734

2021-02-26

Abstract:Magnetic material is considered to as a major concern material for the enrichment of histidine-rich proteins (His-proteins) via metal-ion affinity. In this work, magnetic polymer microspheres with core–shell structure (Fe₃O₄@) were successfully prepared via reflux-precipitation polymerization followed by in situ reduction and growth of Ni²⁺. The obtained Ni nanofoams with flower-like structure and uniform pore size (3.34 nm) provided numerous binding sites for His-proteins. The adsorption performance of Fe₃O₄@ microspheres for His-proteins was estimated via selectively separating bovine hemoglobin (BHb) and bovine serum albumin (BSA) from a matrix composed of BHb, BSA, and lysozyme (LYZ). The results indicated that Fe₃O₄@ microspheres could efficiently and selectively separate His-proteins from the matrix, with a maximum adsorption capacity of ∼2660 mg/g for BHb. Moreover, Fe₃O₄@ microspheres exhibited good stability and recyclability for BHb separation over seven cycles. Therefore, this work reported a novel and facile strategy to prepare core–shell Fe₃O₄@ microspheres, which was promising for practical applications of His-protein separation and purification in proteomics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c19734?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c19734</a>.TEM image of Fe₃O₄ microspheres composed of primary nanocrystals which was about 5 nm in diameter (Figure S1); TGA curves of Fe₃O₄@PMAA and Fe₃O₄@ microspheres (Figure S2); the fitting curves of Langmuir model and Freundlich model for the BHb adsorption isotherm of Fe₃O₄@ microspheres (Figure S3); the adsorption isotherms of Fe₃O₄@PMAA and Fe₃O₄@PMAA/Ni²⁺ microspheres for His-proteins BHb (Figure S4); TEM images of Fe₃O₄@ compositions (Figure S5); EDX analysis of Fe₃O₄@PMAA/Ni²⁺ and Fe₃O₄@ (Figure S6); ICP-MS testings of weight percentage of Ni element and XPS analysis of surface Ni element content of Fe₃O₄@PMAA/Ni²⁺ and Fe₃O₄@ (Figure S7) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c19734/suppl_file/am0c19734_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology