Study on the Preparation and Process Parameter-Mechanical Property Relationships of Carbon Fiber Fabric Reinforced Poly(Ether Ether Ketone) Thermoplastic Composites

Yan Wang,Yanchao Yang,Hongbo Zhang,Siwen Ding,Ting Yang,Jinhui Pang,Haibo Zhang,Jinling Zhang,Yunhe Zhang,Zhenhua Jiang

DOI: https://doi.org/10.3390/polym16070897

IF: 5

2024-03-26

Polymers

Abstract:Carbon fiber fabric-reinforced poly(ether ether ketone) (CFF-PEEK) composites exhibit exceptional mechanical properties, and their flexibility and conformability make them a promising alternative to traditional prepregs. However, the formation of the CFF-PEEK composite is trapped in the high viscosity of PEEK, the smooth surface, and tightly interwoven bundles of CFF. It is more difficult for the resin to flow through the fibers of complex textile structures. Here, a simple film stacking method using the hot-pressing process of plain-woven CFF-PEEK thermoplastic composites is discussed. The uniform distribution of PEEK resin between each layer of CFF reduces the flow distance during the molding process, preventing defects in the composite material effectively. Four process parameters, including molding temperature (370, 385, 400, and 415 °C), molding pressure (1, 2, 4, 8, and 10 MPa), molding time (10, 20, 30, 40, 60, and 90 min), and pre-compaction process, are considered. Interlaminar shear strength (ILSS), tensile strength, and flexural strength of CFF/PEEK composites are evaluated to optimize the process parameters. Moreover, ultrasonic scanning microscopy and scanning electron microscopy are employed to observe the formation quality and microscopic failure modes of CFF/PEEK composites, respectively. The ultimate process parameters are a molding temperature of 410 °C, molding pressure of 10 MPa, molding time of 60 min, and the need for the pre-compaction process. Under the best process parameters, the ILSS is 62.5 MPa, the flexural strength is 754.4 MPa, and the tensile strength is 796.1 MPa. This work provides valuable insight for studying the process parameters of fiber fabric-reinforced thermoplastic polymer composites and revealing their impact on mechanical properties.

polymer science

What problem does this paper attempt to address?

This paper attempts to address the issues encountered in the preparation of carbon fiber fabric reinforced polyether ether ketone (CFF-PEEK) composites, particularly how to ensure the molten PEEK resin fully impregnates the carbon fiber bundles. Specifically, the paper explores the effects of hot pressing process parameters (including molding temperature, pressure, time, and pre-compaction process) on the mechanical properties of CFF-PEEK composites and optimizes these parameters to enhance the performance of the composites.

The study employed a film stacking method combined with a hot pressing process to prepare CFF-PEEK laminated composites and experimentally analyzed the mechanical properties such as interlaminar shear strength (ILSS), tensile strength, and flexural strength of the composites under different hot pressing parameters. The optimal process parameters were determined to be: molding temperature 410°C, molding pressure 10 MPa, molding time 60 minutes, and the need for a pre-compaction process. Under the optimal process parameters, the ILSS of the composite reached 62.5 MPa, the flexural strength reached 754.4 MPa, and the tensile strength reached 796.1 MPa.

This work provides valuable insights into the process parameters of fiber fabric reinforced thermoplastic polymer composites and their impact on mechanical properties.