Characterization, Mechinical, Thermal And Ablative Properties Of Ceramic Modified Phenolic Resin Aerogels Synthsized By Ambient Pressure Drying
Jun Zhang,Rongying Yin,Haiming Cheng,Changqing Hong,Xinghong Zhang,Songhe Meng
2017-01-01
Abstract:During the past few decades, various organic aerogels (AGs) have been synthesized and shown a number of exceptional and even unique properties, such as low bulk density, high porosity, great surface areas, and extremely low thermal conductivity, which enable them being the focus of industry and academia. Thus, AGs exhibit substantial performance boosts in numerous applications such as adsorption, separation, catalysis, energy conversion and storage, and so on. Regrettably, AGs generally exhibit high cost, poor thermal and mechanical properties, which seriously restrict their large-scale applications. In this study, ceramic was introduced into commercial available resin derived aerogel due to the enhancement of silicon to thermal stability and low cost of the resin. Silica ceramic modified phenolic resin (PR-SiO2) aerogel was synthesized by a simple sol-gel polymerization of ceramic precursor, PR, hexamethylenetetramine in an ethylene glycol solution, followed by solvent exchange and ambient pressure drying. The modified effect on the porous structure, textural property, and thermal stability was studied by scanning electron microscope (SEM), nitrogen adsorption isotherms, and thermogravimetric analysis (TGA). According to the characterizations of SEM and nitrogen adsorption, the obtained PR-SiO2 hybrid aerogels have a continuous three dimensional network that consists of phenolic nano-particles and curved nano-sheets with size from 50 to 90 nm, which define numerous mesopores and macropores. TGA in argon atmosphere indicated that the thermal stability of the PR-SiO2 aerogels (both maximum decomposition rate and char yield at 1000 degrees C) is better than that of the pristine PR aerogel. In order to improve the mechanical properties, carbon fabric reinforced aerogel composite was prepared by impregnating carbon-bonded carbon fiber (CBCF) composite with the aerogels. In the micrographs of the aerogel matrix composite, the aerogels are fully and uniformly occupied the void between carbon fibers, and coated with a thin layer on the fiber surface. Moreover, a homogeneous morphology without cracking and fracture was obtained at the fiber/resin interface, as the appropriate porous structure and enough strength of the aerogel networks to decrease and withstand the capillary pressure at the liquid/gas interface during the drying at ambient pressure, prevent the aerogel networks from collapse. Due to the low bulk density (0.18g/cm(3)), high porosity (similar to 90%) and unique fiber geometry (a typical 2D planar random structure with the carbon fibres in the xy direction are distributed homogeneously in plane, while in the z direction over the height of the composite) of the CBCF fabric, the obtained composite possessed low bulk density (0.32- 0.45 g/cm(3)), high compressive strength (0.8-2.8 MPa for different directions) and low thermal conductivity (0.098-0.148 W/(mK)). More importantly, good thermal ablative and insulative properties in oxy-acetylene flame simulated high temperature environment (linear ablation rate as low as 0.085 mm/s, internal temperature peaks below 200 degrees C at 38 mm in-depth position as the surface temperature approximately 1800 degrees C). Therefore, the novel lightweight aerogels and composites are excellent heat-insulation and thermal-protection materials with applications in the fields of energy-saving and aerospace.