Tuning the magnetocaloric properties of lanthanum–strontium manganite by rare-earth Nd3+ doping

A. M. Bolarín-Miró,C. A. Taboada-Moreno,C. A. Cortés-Escobedo,F. Sánchez-De Jesús

DOI: https://doi.org/10.1007/s10973-024-13565-y

IF: 4.755

2024-09-04

Journal of Thermal Analysis and Calorimetry

Abstract:This study investigated the effect of neodymium (Nd) on the crystal structure and magnetocaloric properties of lanthanum–strontium manganites (La 0.7−x Nd x Sr 0.3 MnO 3, 0 ≤ x ≤ 0.4), synthesized by assisted high-energy ball milling. Rietveld analysis from X-ray diffraction disclosed that Nd 3+ did not promote crystallographic phase transitions. The rhombohedral crystal structure remained in the R -3 c space group for all the compositions, with slight changes in lattice parameters. The defect model allowed the quantification of the Mn 4+ occupancy, which is in the range from 0.20 to 0.26 mol, for 0.1 and 0.4 mol of Nd 3+ , respectively. The presence of Mn 4+ promoted further ferromagnetic interactions, increasing systematically the saturation magnetization, from 65 A·m 2 ·kg −1 to 73 A·m 2 ·kg −1 , and a diminution in the Curie temperature from 364 to 255 K, for 0 and 0.4 mol of Nd 3+ , respectively, obtained by temperature-dependent magnetization measurements. The doped manganite with 0.35 mol of Nd 3+ showed a maximum of entropy change of 3.73 Jkg −1 K −1 at 1.8 T near room temperature, with a relative cooling power of 82 Jkg −1 and temperature-averaged entropy change, TEC(3) and TEC(10), of 3.53 and 3.06 Jkg −1 K −1 , respectively. It is demonstrated that the presence of Nd 3+ modulates the Curie temperature near room temperature and enhances the magnetocaloric properties at low magnetic fields, making these manganites a promising material for magnetocaloric applications.

chemistry, physical, analytical,thermodynamics