Tuning magnetic and table-like magnetocaloric effect of La0.6−xErxSr0.4MnO3(x = 0.0125, 0.05, 0.1) manganites

Tina Raoufi,Ali Ghotbi Varzaneh,Mohammad Hossein Ehsani,Enke Liu,Volodymyr Chernenko

DOI: https://doi.org/10.1016/j.materresbull.2022.111997

IF: 5.6

2022-12-01

Materials Research Bulletin

Abstract:Polycrystalline samples of La0.6−xErxSr0.4MnO3 (x = 0.0125, 0.05, 0.1) have been prepared using the solid-state reaction method. X-ray powder diffraction confirmed a single-phase state and revealed a rhombohedral structure with the R ̄3c space group in all samples. It is shown that the unit cell volume gradually decreases by replacing La with Er. The Curie temperature (Tc) decreases as the Er content rises. A downturn of the reciprocal value of the magnetic susceptibility versus temperature curve proves the presence of the Griffith phase above Tc. An occurrence of two overlapped transitions, from the ferromagnetic phase to the Griffith phase and from the latter one to the paramagnetic phase, in La0.6−xErxSr0.4MnO3 samples caused the significant expansion of the total transition temperature range as x increased. In turn, a widening of the transition temperature span gives rise to the spreading of the magnetic field induced entropy maximum over a broad temperature interval, resulting in a considerable enhancement of the relative cooling power.

materials science, multidisciplinary