Ratcheting-induced Twinning/de-Twinning Behaviors in a 316LN Austenitic Stainless Steel
Wen-hao Yang,Peng-ming Cheng,Yang Li,Ruihong Wang,Gang Liu,Lu Xin,Jin-yu Zhang,Jun Sun
DOI: https://doi.org/10.1016/j.msea.2022.143648
2022-01-01
SSRN Electronic Journal
Abstract:Although the evolution of dislocation substructure during ratcheting deformation has been previously studied in 316LN austenitic steel, studies on ratcheting-induced twinning and de-twinning behaviors are very scarce. In this paper, microstructural evolutions, especially the twinning/de-twinning behaviors, were systematically investigated in a 316LN austenitic steel under ratcheting cycling. Different peak stresses (320, 400, 450, and 500 MPa) were deliberately designed to demonstrate a potential correlation between the twinning/de-twinning and the dislocation pattern. The experimental results showed that, at the low peak stress of 320 MPa, annealing twins were quite stable and the dislocation pattern mainly consisted of planar dislocation arrangement. Raising the peak stress to 400 MPa, most of the annealing twins were gradually de-twinned and the dislocation pattern displayed a different feature prevailed by dislocation veins, walls and cells. As the peak stress reaches 450 MPa and in particular up to 500 MPa, the annealing twins get quickly de-twinned, while stacking faults and deformation twins were induced besides the dislocations. The critical stress to trigger deformation twins in the 316LN austenitic steel was evaluated to be around 500 MPa, which is in broad agreement with the experimental results. This indicates that the nucleation of deformation twins under ratcheting cycles should be controlled by the peak stress rather than the accumulation strain. An additional cycling hardening stage was observed in the ratcheting cycling response under the peak stress of 450 and 500 MPa, which should be closely related to the formation of stacking faults and deformation twins. Moreover, the stress-dependent de-twinning of annealing twins were discussed in terms of dislocation interaction with annealing twins.