Research on Laser Cleaning Technology for Aircraft Skin Surface Paint Layer

Jinxuan Li,Jianjun Yang,Jiaxuan Liu,Hui Chen,Yunfei Duan,Xinjian Pan
DOI: https://doi.org/10.3390/ma17102414
IF: 3.4
2024-05-18
Materials
Abstract:In this study, a pulsed laser operating at a wavelength of 1064 nm and with a pulse width of 100 ns was utilized for the removal of paint from the surface of a 2024 aluminum alloy. The experimental investigation was conducted to analyze the influence of laser parameters on the efficacy of paint layer removal from the aircraft skin's surface and the subsequent evolution in the microstructure of the laser-treated aluminum alloy substrate. The mechanism underlying laser cleaning was explored through simulation. The findings revealed that power density and scanning speed significantly affected the quality of cleaning. Notably, there were discernible damage thresholds and optimal cleaning parameters in repetitive frequency, with a power density of 178.25 MW/cm2, scanning speed of 500 mm/s, and repetitive frequency of 40 kHz identified as the primary optimal settings for achieving the desired cleaning effect. Thermal ablation and thermal vibration were identified as the principal mechanisms of cleaning. Moreover, laser processing induced surface dislocations and concentrated stress, accompanied by grain refinement, on the aluminum substrate.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
The paper investigates the technique of using a 1064 nm pulsed laser to remove the surface coating of 2024 aluminum alloy. The objective of the study is to optimize the laser parameters (power density, scanning speed, and repetition frequency) to improve the cleaning effect and reduce damage to the substrate. In the experiment, the researchers evaluate the cleaning effect by quantifying the roughness and material removal rate, and analyze the microstructural changes of the aluminum alloy substrate after laser treatment. The paper indicates that power density and scanning speed significantly affect the cleaning quality. There exists an optimal repetition frequency threshold, where the ideal cleaning effect is achieved with a power density of 178.25 MW/cm², a scanning speed of 500 mm/s, and a repetition frequency of 40 kHz. The main cleaning mechanisms are thermal evaporation and thermal vibration. Laser treatment results in surface dislocations and stress concentration on the aluminum alloy substrate, accompanied by grain refinement. Furthermore, the paper establishes a 2D transient temperature and stress field model based on COMSOL Multiphysics to simulate the laser cleaning process. Replica samples of actual aircraft skins are used as experimental materials, and laser cleaning tests are conducted with different parameters. The influence of process parameters is analyzed by comparing the cleaning area, depth, and roughness under different parameters. The results indicate that as the laser power density increases, the surface roughness initially decreases and then increases. When a certain threshold is reached, the substrate surface is damaged. The paper also discusses the impact of scanning speed on the cleaning effect, finding that the speed is related to the point overlap rate, which affects the cleaning quality and substrate damage. By adjusting these parameters, laser cleaning conditions can be found that effectively remove the coating while minimizing damage to the substrate.