Abstract:With the purpose of further investigating the influence of aging on the tensile behaviors of hydroxyl-terminated polybutadiene (HTPB) propellant at low temperatures under dynamic loading, uniaxial tensile stress responses of thermal accelerated aged propellant samples at different temperatures (223–298 K) and strain rates (\(0.40\mbox{--}42.86~\mbox{s}^{-1}\)) were obtained through the use of a new INSTRON testing machine. And scanning electron microscope (SEM) was employed to analyze the microscopic damage of HTPB propellant under the test conditions. Test results indicate that aging can significantly affect the characteristics of the stress-strain curves, mechanical properties and fracture mechanisms of HTPB propellant at low temperatures under dynamic loading. There are three regions in the tensile stress-strain curves of aged propellant when deforming at lower temperatures and the highest strain rate, however, there are five ones for unaged propellant. At lower temperatures and higher strain rates, the strain at maximum tensile stress of the propellant decreases more obviously after aging. Moreover, the variation of mechanical parameters for HTPB propellant with aging time are highly complex due to the occurrence of oxidative cross-linking during aging and the distinct changes of the fracture mechanisms. These variation were reasonably well described with linear model and the improved exponential model in this investigation. The fracture mechanism of aged propellant can change from dewetting, matrix tearing and AP particle fracture to only AP particle fracture with increasing strain rate for the entire test temperature range, and the strain rate for this transition is all at \(4.00\mbox{--}14.29~\mbox{s}^{-1}\). In addition, the microscopic damage of HTPB propellant becomes more severe with the thermal aging time rising, however, this effect is weaker at higher strain rates after long-time thermal aging. Finally, the master curves of typical mechanical parameters for aged HTPB propellant were constructed according to the time-temperature superposition principle (TTSP).

Degradation Laws and Characteristic Parameters of Performance of Gun Propellant in Storage

Test Study on Storage Aging Properties of HTPB Propellants

Experimental Investigation on the Influence of Confining Pressure on Thermal Aged CMDB Propellant

Storage Aging Analysis Of Electric Initiator By Aging Test

Reliability Calculation of Solid Propellant Based on Accelerated Degradation Test

Simulation of interior ballistic two-phase flow of storage propellant charge

Effect of Accelerated Cyclic Aging on the Ballistic Properties of Composite Solid Propellant

Molecular Dynamics Study on Aging Mechanism of HTPB Propellants

Reaction Model for the Aging and Shelf‐Life Prediction of Double‐Base Propellant SF‐3

Storage-life prediction and relationship between maximum elongation and stabilizer depletion for a composite modified double base propellant (CMDB) propellant

A constitutive model of solid propellants considering aging and confinement pressure

Tensile Behaviors of Thermal Aged HTPB Propellant at Low Temperatures under Dynamic Loading

Research on the Aging Properties of HTPB Propellant under Vacuum

Study on Dynamic Impact and Ignition Response Behavior of GAP/PET/RDX Based Propellant

Analytical Methods for Stability Assessment of Nitrate Esters-Based Propellants

Multiscale damage evolution and fracture for thermal aging energetic material based on mesoscopic observation and molecular dynamics simulation

A One-Dimensional Model for the Aging and Damage Effects on the Response of Composite Double-Base Propellants

Research on the Thermal Aging Performance of a GAP-Based Polyurethane Elastomer

A review on the effect of ageing on the ballistic properties of solid gun and rocket propellants

A non-calorimetric approach for investigating the moisture-induced ageing of a pyrotechnic delay material using spectroscopies

Relaxation Properties of the Solid Propellant Based on Hydroxyl-Terminated Polybutadiene