Carbon nanotube composite membranes of brominated poly (2, 6-diphenyl-1, 4-phenylene oxide) for gas separation

Hailin Cong, Jianmin Zhang, Maciej Radosz, Youqing Shen
2007-05-15
Abstract:The mechanical strength of polymeric membranes is one of the limitations in their applications. Carbon nanotubes (CNTs) are very effective in reinforcing polymeric materials, but it is unknown whether they degrade the membranes’ gas separation performance. Using brominated poly(2,6-diphenyl-1,4-phenylene oxide) (BPPOdp) as an example, we show that pristine single-wall CNTs (SWNTs) and multi-wall CNTs (MWNTs) formed polymeric nanocomposite membranes with BPPOdp. The composite membranes had an increased CO2 permeability but a similar CO2/N2 selectivity compared to the corresponding pure-polymer membrane. The CO2 permeability increased with increasing the CNT content and reached a maximum of 155Barrer at 9wt% of SWNTs, or 148Barrer at 5wt% of MWNTs. The CO2/N2 separation performance was insensitive to the MWNT diameter or length. Carboxylic acid-functionalized …
What problem does this paper attempt to address?