Nucleation-Controlled Growth of High-Quality CsPbBr3 Single Crystal for Ultrasensitive Weak-Light Photodetector
Xiao Zhao,Shimao Wang,Fuwei Zhuge,Nengwei Zhu,Yanan Song,Mengyu Fu,Zanhong Deng,Xiaodong Fang,Gang Meng
DOI: https://doi.org/10.1039/d3tc00550j
IF: 6.4
2023-05-16
Journal of Materials Chemistry C
Abstract:All inorganic perovskite CsPbBr 3 single crystal (SC) possessing both excellent photoelectric properties and environmental stability has become a promising photoelectric material. However, it remains challenging to prepare high-quality CsPbBr 3 SC with regular shape through solution growth method due to the difference in growth rates along different crystal orientations and the difficulty in controlling the number of nucleation seeds. In this work, solution refinement has been introduced into the choline bromide assisted inverse temperature crystallization method for achieving high-quality cuboid-shaped CsPbBr 3 SC. The acquired CsPbBr 3 SC exhibits a relatively low trap density of 4.02 × 10 9 cm −3 , and a relatively high carrier mobility of 89.72 cm 2 V −1 s −1 . Furthermore, the as-grown CsPbBr 3 SC based photodetector exhibits high photodetection performance, especially ultrasensitive weak light detection performance. Under the 530 nm light irradiation with a low light power density of 0.11 μW cm −2 , the responsivity, external quantum efficiency, and detectivity of CsPbBr 3 SC based photodetector at the bias of 10 V could reach 36.4 A W −1 , 8520%, and 1.34 × 10 14 Jones, respectively, and a fast response speed with a rise time of 1.36 μs and a fall time of 6.38 μs has been achieved. It is worth noting that the photodetector exhibits an extremely low detection limit of 2.25 nW cm −2 , indicating the great potential for weak light detection.
materials science, multidisciplinary,physics, applied