The Electronic Impact of Light-Induced Degradation in CsPbBr 3 Perovskite Nanocrystals at Gold Interfaces

Azmat Ali,Herve Cruguel,Erika Giangrisostomi,Ruslan Ovsyannikov,Mathieu G. Silly,Lenart Dudy,Ute B. Cappel,Emmanuel Lhuillier,Nadine Witkowski,Fredrik O. L. Johansson
DOI: https://doi.org/10.1021/acs.jpclett.4c00139
IF: 6.888
2024-03-29
The Journal of Physical Chemistry Letters
Abstract:The understanding of the interfacial properties in perovskite devices under irradiation is crucial for their engineering. In this study we show how the electronic structure of the interface between CsPbBr(3) perovskite nanocrystals (PNCs) and Au is affected by irradiation of X-rays, near-infrared (NIR), and ultraviolet (UV) light. The effects of X-ray and light exposure could be differentiated by employing low-dose X-ray photoelectron spectroscopy (XPS). Apart from the common degradation product...
chemistry, physical,physics, atomic, molecular & chemical,nanoscience & nanotechnology,materials science, multidisciplinary
What problem does this paper attempt to address?
This paper aims to explore the changes in the electronic structure of cesium - lead - bromide perovskite nanocrystals (CsPbBr₃ PNCs) on the gold interface (Au) when irradiated by near - infrared light (NIR), ultraviolet light (UV) and X - rays, as well as the resulting photodegradation phenomena. Specifically, the researchers focused on how these different types of illumination conditions affect the interaction between CsPbBr₃ PNCs and the Au interface, and observed the formation of a new intermediate product (Pbint) through low - dose X - ray photoelectron spectroscopy (XPS) technology. ### Main problems in the paper 1. **Interface stability under illumination conditions**: - Through experimental observations, the researchers found that under high - intensity X - ray or UV light irradiation, irreversible damage occurs between CsPbBr₃ PNCs and the Au interface, manifested as the appearance of two new chemical species in the Pb 4f spectrum: metallic lead (Pb⁰) and an intermediate product (Pbint) located between Pb²⁺ and Pb⁰. 2. **Formation mechanism of Pbint**: - Pbint is considered to be a monolayer of metallic lead formed by the release of Pb²⁺ ions due to the destruction of the perovskite structure and underpotential deposition (UPD) on the Au surface. This process requires the activation of high - energy photons (such as high - energy X - rays or UV light), while low - intensity X - rays and NIR light require longer - term high - intensity irradiation to observe the formation of Pbint. 3. **Effect of illumination conditions on PNCs**: - The study found that the effect of NIR light irradiation on PNCs is relatively small, but long - term high - intensity irradiation can also cause the movement of Pb²⁺ to a higher binding energy and the appearance of a small amount of Pbint. In contrast, UV light irradiation can cause more significant changes, including a large shift in the binding energy of Pb²⁺ and the formation of Pb⁰ and Pbint. ### Main conclusions - **Effect of illumination conditions on CsPbBr₃ PNCs**: High - energy X - ray and UV light irradiation can cause irreversible damage between CsPbBr₃ PNCs and the Au interface, forming new chemical species Pbint and Pb⁰. - **Formation mechanism of Pbint**: The formation of Pbint is due to the release of Pb²⁺ ions caused by the destruction of the perovskite structure and underpotential deposition (UPD) on the Au surface. - **Effect of NIR light**: The effect of NIR light irradiation on PNCs is relatively small, but long - term high - intensity irradiation can also cause some changes. Through these studies, the author emphasizes the need to consider the influence of illumination conditions on the stability and performance of materials when designing devices based on perovskite materials, especially in the case of contact with metals such as gold.