Synthesis and Electrochemical Properties of Intercalated Polyaniline Nanowire Composites
Biao Wang,Dingzhi Chen,Anning Ma,Yu Zheng,Shuhao Deng
DOI: https://doi.org/10.11933/j.issn.1007-9289.20211208003
2023-01-01
China surface engineering
Abstract:Conductive polyaniline(PANI) is characterized by a high conductivity, easy doping, reversible electrochemical activity, good uniformity, good thermal stability, and high stability in air. Additionally, it has a high potential for application in batteries and other fields. However, PANI exhibits different morphologies, structures, and performances when synthesized under different conditions. Nanoscale PANI composites have promising applications in the development of small, lightweight, and convenient devices. Among them, PANI composites with a nanowire structure are conducive for electron transfer because of the reduced ion diffusion distance and migration, which provides the optimal energy storage effect for use as an electrode material in batteries. Presently, conductive PANI with a nanowire structure is typically prepared using a hard or soft template method. Based on the defects of the template method, a simple, fast, and low-cost method was proposed to synthesize uniform-sized PANI nanowire composites and study their electrochemical performance. The synthesis of PANI nanowire composites was a two-step process. The first step involved the electrochemical stripping of the graphite plates. An anodic oxidation stripping method was used to prepare a rough surface graphite plate in a nitric acid, phosphoric acid reduction, and sulfuric acid system. The second step included the polymerization of the PANI to obtain a PANI nanowire composite, which was performed on a graphite plate after electrochemical stripping treatment. The results showed that the surface roughness, layer spacing, and specific surface area of the graphite plates were increased after electrochemical stripping. Additionally, the XRD and FI-IR analyses revealed that graphene oxide and graphene were generated on the surface of the electrochemically-peeled graphite plates, thereby providing many active points for the electropolymerization process in the second step. Using an SEM analysis, the micromorphology of the PANI composite(PANI / GO) synthesized using a nitric acid system was found to be a three-dimensional network structure composed of nanowires with a diameter of approximately 100 nm. The micromorphology of the PANI composite synthesized using a phosphoric acid reduction system (PANI / GR1) was a mixture of nanosheets and nanowires with a diameter of approximately 50 nm, whereas that of the PANI composite synthesized using a sulfuric acid system(PANI / GR2) was nanowires with a diameter of approximately 80 nm. Subsequently, the electrochemical properties of the PANI composites were investigated. First, their energy storage properties were studied using a simple seawater battery that was prepared using a magnesium alloy and a PANI composite material as the electrodes. The battery started discharging at a current density of 3.75 mA & BULL;cm-2 and stopped at 0.9 V, and the specific energies were 540, 228 and 363 mWh & BULL;g-1. The results showed that PANI / GO exhibited the optimal energy-storage performance. Subsequently, Tafel curves and AC impedance diagrams were used to analyze the electrochemical properties of the three PANI composites, where a larger reaction current density and smaller Tafel curve slope angle was found to produce a semi-circle with a smaller diameter. The steep slope of the AC impedance diagram indicates that the polarization of the battery reaction of the PANI / GO composite electrode is the lowest, its reaction speed is the fastest, and its electrochemical performance is optimal owing to its excellent conductivity, stability, and large specific surface area, which are conducive for providing a sufficiently close approach with the electrolyte and promoting the transmission and diffusion of ions. Therefore, the proposed PANI / GO nanowire composite can be used as battery cathode material. Moreover, its preparation method provides a theoretical and practical basis for the controllable synthesis of other conductive polymer composites.