Abstract:The incorporation of metakaolin into cementitious materials could improve the compressive strength and durability of cement paste, which are correlated well with the hydration behavior of cement-metakaolin blended mixture. The aim of this work is to reveal the coupled effects between the cement hydration and the pozzolanic reaction of metakaolin during the early stage, the methodologies including fluidity, setting time, compressive strength were employed to measure the properties of cement paste, while another methodologies, such as conductivity, Mercury Intrusion Porosimetry (MIP), Thermogravimetric (TG), X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were adopted to investigate the hydration behavior and microstructure characterization. The results indicated that the fluidity of fresh cement paste decreased sharply with the increase of metakaolin, and the addition of superplasticizer could improve the fluidity of fresh cement paste effectively. The setting times of fresh cement paste were delayed slightly with the incorporation of metakaolin. The conductivity of cement suspension dropped gradually with the increase of metakaolin during the early stage, meaning the hindrance to the ion dissolution from cement-metakaolin blended mixture. The compressive strength increased slightly with the addition of metakaolin at 1 d, while it increased remarkably at 3 d. The results of MIP presented that the pore structure was refined with the increase of metakaolin at 3 d. The TG results showed that the incorporation of metakaolin promoted the formation of hydration products at 3 d. The XRD results presented that calcium hydroxide (CH) decreased with the addition of metakaolin, which may be consumed by the pozzolanic reaction of metakaolin. SEM observation confirmed that the microstructure of cement paste became much denser with the increase of metakaolin, which was in good agreement with the results of compressive strength and MIP measurement.

The Investigation about Gel Properties of New Composite Materials with Meta-kaolin

Early-Stage Geopolymerization Process of Metakaolin-Based Geopolymer

Compositional Dependence of Pore Structure, Strengthand Freezing-Thawing Resistance of Metakaolin-Based Geopolymers

Influence of Metakaolin on the Properties of Hydroxyethyl Methyl Cellulose Modified Mortar

The Relationships Between Stress and Strain for High-Performance Concrete with Metakaolin

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Preparation and properties of metakaolin-fumed-silica geopolymer modified with sodium silicate and potassium silicate activators

Effects of Different Calcium Sources on Mechanical Properties of Metakaolin Geopolymers

Influence of metakaolin on the conversion and compressive strength of quaternary phase paste

Experimental Study on the Mechanical Properties and Microstructure of Metakaolin-Based Geopolymer Modified Clay

Geopolymer concrete with metakaolin for sustainability: a comprehensive review on raw material’s properties, synthesis, performance, and potential application

Influence of metakaolin on the hydration and microstructure evolution of cement paste during the early stage

Drying Shrinkage and Microstructural Evolution of Concrete with High-Volume and Low-Grade Metakaolin

Correlating the Elastic Properties of Metakaolin-Based Geopolymer with Its Composition

Mechanical Properties and Reaction Kinetics of Alkali-Activated Metakaolin

Relationships of Uniaxial Compressive Stress-Strain for High Performance Concrete with Metakaolin

Influence of GGBFS and silica fume on characteristics of alkali-activated Metakaolin-based concrete

Rheological and mechanical properties of aluminosilicious cementitious materials as refractory castable binders

Mechanical property and microstructure of quaternary phase paste blended with metakaolin

Mechanical performance and hydration mechanism of geopolymer composite reinforced by resin

Strength and Pore Structure Development of High-Plasticity Clay Treated with MK-Blended Cement