Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

A bio-based reprocessable and degradable polybenzoxazine with acetal structures

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Biobased Polybenzoxazine Vitrimer with Imine Bonds: Shape Memory, Reprocessing, and Degradation

High Heat-Resistant and Degradable Polybenzoxazines with a Diacetal Structure

Preparation and Performances of Degradable Polybenzoxazine by Ring-Opening Metathesis Polymerization

Nature's Empowerment: Unraveling Superior Performance and Green Degradation Closure in Self-Curing Fully Bio-based Benzoxazine

A Bio-Based Polybenzoxazine Derived from Diphenolic Acid with Intrinsic Flame Retardancy, High Glass Transition Temperature and Dielectric Properties.

Sustainable Preparation of Bio-Based Polybenzoxazine Resins from Amino Acid and Their Application in CO2 Adsorption

Bio-based epoxy resins derived from diphenolic acid via amidation showing enhanced performance and unexpected autocatalytic effect on curing

Film-forming Characteristics and Thermal Stability of Low Viscosity Benzoxazines Derived from Melamine

Fully Bio-Based Acetal Diepoxy Monomers: High Modulus, Good Thermal Stability and Readily Degradability

Synthesis, polymerization and thermal properties of bio‐based benzoxazine resins containing imide or amide functionality

Design of rectifiable bio-based polybenzoxazine for stimulated self-healing and shape memory applications with antimicrobial activity

Facile preparation of reprocessable and degradable phenolic resin based on dynamic acetal motifs

Degradable benzyl cyclic acetal epoxy monomers with low viscosity: Synthesis, structure-property relationships, application in recyclable carbon fiber composite

Synthesis of bio‐diamine derived main‐chain type benzoxazine resins with low surface free energy

Synthesis, Characterization, and Polymerization of A Novel Benzoxazine Based on Diethyltoluenediamine

An M‐phenylenediamine‐based Benzoxazine with Favorable Processability and Its High‐performance Thermoset