Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Synthesis, Characterization, and Polymerization of A Novel Benzoxazine Based on Diethyltoluenediamine

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

An M‐phenylenediamine‐based Benzoxazine with Favorable Processability and Its High‐performance Thermoset

Novel Thermally Stable and Organosoluble Aromatic Polyamides with Main Chain Phenyl-1,3,5-Triazine Moieties

Preparation, Curing Kinetics, and Properties of a Novel Low-Volatile Starlike Aliphatic-Polyamine Curing Agent for Epoxy Resins

Polymerization Scheme and Chemical Structure of Aromatic Diamine‐Based Polybenzoxazines: New Details

Kinetics and properties of diethyltoluenediamine type benzoxazine-cured diglycidyl ether of bisphenol-A

Synthesis, ring-opening polymerization, and properties of benzoxazines based on o- and p-hydroxybenzyl alcohols

Synthesis, characterization and self-promoted cure behaviors of a new phthalonitrile derivative 4-(4-(3, 5-diaminobenzoyl) phenoxy) phthalonitrile

Synthesis of phosphaphenanthrene-functional monobenzoxazine for enhancing thermal properties of polybenzoxazine thermosets

Diethylphosphonate-Containing Benzoxazine Compound As A Thermally Latent Catalyst and A Reactive Property Modifier for Polybenzoxazine-Based Resins

A Bio-Based Polybenzoxazine Derived from Diphenolic Acid with Intrinsic Flame Retardancy, High Glass Transition Temperature and Dielectric Properties.

A Novel Post-Polymerization Modification Route to Functional Poly(Disubstituted Acetylenes) Through Phenol-yne Click Reaction

Thiophene-Rich Benzoxazines with an Amide Moiety: Integration of Structural and Hydrogen Bonding Influence on the Polymerization Mechanism by Experimental and Computational Studies

Synthesis of Daidzein and Thiophene Containing Benzoxazine Resin and Its Thermoset and Carbon Material

Film-forming Characteristics and Thermal Stability of Low Viscosity Benzoxazines Derived from Melamine

Polymerization behaviors and properties of benzoxazine resins based-on meta-substituted anilines

Synthesis and characterization of novel bio-based benzoxazines from eugenol