Abstract:Solid oxide electrolysis cells (SOECs) are promising devices for CO2 and H2O co-electrolysis into syngas. Degradation occurring within SOECs is still of great concern for their commercial deployment. Therefore, it is important to understand the degradation mechanisms and optimize SOEC long-term operation. A 1-dimensional (1D) pseudo-dynamic model was developed for SOEC operating under CO2/H2O co-electrolysis and implemented in Aspen Plus® using Fortran® routines. The structural degradation of a typical SOEC material set: Ni-YSZ cathode, YSZ electrolyte and LSM-YSZ anode were also accounted for. The model was dynamically validated for different current densities (0.5, 0.75 and 1.0 A/cm2). The effects of operating conditions and structural degradation on SOEC long-term electrochemical performance and syngas production are assessed. Performance prediction indicated that increasing the current density and operating temperature initially enhance SOEC performance. However, the operating voltage increases at faster rates at higher current densities and temperatures causing the syngas production efficiency to decrease due to higher power utilisation. Long-term SOEC degradation is mostly due to LSM-YSZ anode delamination with a degradation rate of 3.96 %/1000hrs at 750 °C, 1 bar and 1.5 A/cm2. Applying an anti-oxidant layer on the interconnect surface and adjusting La/Sr ratio in the A-site of LSM considerably reduce the degradation rate by roughly 78% at the anode.

Degradation of flat-tube solid oxide electrolytic stack for co-electrolysis of H 2 O and CO 2 under pulsed current

Performance and degradation of an SOEC stack with different cell components

Dynamic Behavior of High-Temperature CO2/H2O Co-Electrolysis Coupled with Real Fluctuating Renewable Power

Solid Oxide Electrolysis Cell under Real Fluctuating Power Supply with a Focus on Thermal Stress Analysis

Durability of solid oxide electrolysis stack under dynamic load cycling for syngas production

Long‐Term Behavior of a Solid Oxide Electrolyzer (SOEC) Stack▴

Electrochemical Analysis of an Electrolyte-Supported Solid Oxide Cell-Based MK35x Stack during Long-Term Electrolysis Operation

Degradation behavior under alternating constant-current/constant-voltage discharge for flat-tube solid oxide fuel cells inside stack

Analysis of Electrochemical Degradation Phenomena of SOC Stacks Operated in Reversible SOFC/SOEC Cycling Mode

Effect of seawater on the performance of flat-tube solid oxide cell for CO2/H2O co-electrolysis

Accelerated degradation for solid oxide electrolysers: Analysis and prediction of performance for varying operating environments

Improved durability of SOEC stacks for high temperature electrolysis

Long-term performance prediction of solid oxide electrolysis cell (SOEC) for CO2/H2O co-electrolysis considering structural degradation through modelling and simulation

Towards strategies to mitigate degradation and regenerate performance of a solid oxide electrolyzer during co-electrolysis operation

Dynamic response characteristics of solid oxide cell stacks for seawater/CO 2 co-electrolysis under strong fluctuation electricity

Analysis of Degradation Phenomena of SOC Stacks Operated in Reversible SOFC / SOEC Cycling Mode

Mechanisms of performance degradation induced by thermal cycling in solid oxide fuel cell stacks with flat-tube anode-supported cells based on double-sided cathodes

A Comparative Study of the Performance and Electrode Processes of Solid Oxide H<sub>2</sub>O Electrolysis and CO<sub>2</sub> Electrolysis

Electrochemical Characterization and Mechanism Analysis of High Temperature Co-electrolysis of CO2 and H2O in a Solid Oxide Electrolysis Cell

Dynamic behavior and control strategy study of CO2/H2O co-electrolysis in solid oxide electrolysis cells