Preparation and Characterization of Nano-CL-20/TNT Cocrystal Explosives by Mechanical Ball-Milling Method

Yubing Hu,Shuo Yuan,Xiaojiang Li,Meng Liu,Fengxi Sun,Yanpeng Yang,Gazi Hao,Wei Jiang

DOI: https://doi.org/10.1021/acsomega.0c02426

IF: 4.1

2020-07-07

ACS Omega

Abstract:Nano-CL-20/TNT cocrystal explosive was successfully prepared by mechanical ball milling with 0.38 mm grinding beads. The micromorphology and particle size of cocrystal explosive were characterized by scanning electron microscopy. The average particle size of nano-CL-20/TNT cocrystal explosive was 119.5 nm and showed a spherical-like micromorphology. The crystal structure of cocrystal explosive was characterized by powder X-ray diffraction, infrared spectroscopy, and Raman spectroscopy. The results show that mechanical ball milling does not change the molecular structure of the raw material, but the sample after ball milling has a new crystal phase, rather than a simple mixing of raw materials. Differential scanning calorimetry tests show that nano-CL-20/TNT cocrystal explosive has a higher decomposition temperature; impact sensitivity tests show that the properties of cocrystal explosive are 26 and 21.7 cm higher than those of CL-20 and CL-20/TNT mixture, respectively, which indicates that nano-CL-20/TNT cocrystal explosive has better thermal stability and safety.This article has not yet been cited by other publications.

chemistry, multidisciplinary

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to prepare nano - scale CL - 20/TNT cocrystal explosives by mechanical ball - milling method and evaluate their properties, especially thermal stability and safety. Specifically, the research aims to: 1. **Preparation method**: Successfully prepare nano - scale CL - 20/TNT cocrystal explosives by mechanical ball - milling method (using 0.38 - millimeter grinding beads). 2. **Characterization of microscopic morphology and particle size**: Observe the microscopic morphology and particle size distribution of the cocrystal explosives by scanning electron microscope (SEM). The results show that the average particle size of the nano - scale CL - 20/TNT cocrystal explosives is 119.5 nanometers and they are spherical. 3. **Characterization of crystal structure**: Analyze the crystal structure of the cocrystal explosives by powder X - ray diffraction (XRD), infrared spectroscopy (IR) and Raman spectroscopy (Raman). The results indicate that mechanical ball - milling does not change the molecular structure of the raw materials, but forms a new crystal phase instead of simply mixing the raw materials. 4. **Thermal stability test**: Differential scanning calorimetry (DSC) test shows that the nano - scale CL - 20/TNT cocrystal explosives have a higher decomposition temperature. 5. **Sensitivity test**: Impact sensitivity test shows that the impact height of the nano - scale CL - 20/TNT cocrystal explosives is 26 centimeters and 21.7 centimeters higher than that of pure CL - 20 and CL - 20/TNT mixture respectively, indicating that it has better thermal stability and safety. In conclusion, this paper mainly solves the problem of how to prepare nano - scale CL - 20/TNT cocrystal explosives by mechanical ball - milling method and verifies its superior performance in terms of thermal stability and safety. This provides new ideas for the future industrial production and application of high - energy explosives.

Preparation and Characterization of Nano-CL-20/TNT Cocrystal Explosives by Mechanical Ball-Milling Method

Towards the Low-Sensitive and High-Energetic Co-Crystal Explosive CL-20/TNT: from Intermolecular Interactions to Structures and Properties

Initial Decomposition of the Co-crystal of CL-20/TNT: Sensitivity Decrease under Shock Loading

Preparation and Molecular Dynamic Simulation of Superfine CL-20/TNT Cocrystal Based on the Opposite Spray Method

Controllable Explosion of Nanobomb by Modifying Nanocontainer and External Shocks

Mechanochemical fabrication and properties of CL-20/RDX nano co/mixed crystals

Thermochemical properties of nanometer CL-20 and PETN fabricated using a mechanical milling method

CL-20-Based Cocrystal Energetic Materials: Simulation, Preparation and Performance

Theoretical investigations on CL‐20/TNBA co-crystal explosive via density functional method and molecular dynamics method

Formation and characterization of core-shell CL-20/TNT composite prepared by spray-drying technique

Preparation and Characterization of A Novel Cocrystal Explosive

Theoretical investigations on stability, sensitivity, energetic performance, and mechanical properties of CL-20/TNAD cocrystal explosive by molecular dynamics method

Morphology and properties of CL-20/MTNP cocrystal prepared via facile spray drying

Preparation of Ultrafine CL‐20 by Wet Grinding Method and the Study on Its Properties

"Thermal escape" of MTNP: the phase separation of CL-20/MTNP cocrystals under long-term heating

Mechanism of the Impact-Sensitivity Reduction of Energetic CL-20/TNT Cocrystals: A Nonequilibrium Molecular Dynamics Study

Preparation and safety study of TKX-50/CL-20 composite explosives

CL-20/TNT decomposition under shock: cocrystalline versus amorphous

Study on mechanical improvement of CL‐20 energetic co‐crystals based PBX by surface modification

Ab Initio Neural Network MD Simulation of Thermal Decomposition of a High Energy Material CL-20/TNT.

Theoretical investigations on a novel CL-20/LLM-105 cocrystal explosive by molecular dynamics method