Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

Temperature effects on hard carbon derived from sawdust as anode materials for sodium ion batteries

Two-step Synthesis of Hard Carbons Anode Material from Poplar Wood with Enhanced Performance for Sodium-Ion Batteries

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

A Life Cycle Assessment of Hard Carbon Anodes for Sodium-Ion Batteries

Sodium‐Ion Batteries: Hard–Soft Carbon Composite Anodes with Synergistic Sodium Storage Performance (adv. Funct. Mater. 24/2019)

Optimizing Hard Carbon Materials for Sodium-Ion Batteries: Insights from Particle Size and Soft Carbon-Coating Strategy

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Development of Biomass‐Derived Hard Carbon for Sodium‐Ion Batteries: Optimizing Microstructure and Electrochemical Performance

Low-Cost and High-Performance Hard Carbon Anode Materials for Sodium-Ion Batteries

Biomass hard carbon of high initial coulombic efficiency for sodium-ion batteries: Preparation and application

High‐Performing All‐Solid‐State Sodium‐Ion Batteries Enabled by the Presodiation of Hard Carbon

Hierarchical porous hard carbon derived from rice husks for high-performance sodium ion storage

Sulfur-doping biomass based hard carbon as high performance anode material for sodium-ion batteries

Hard carbon derived from waste tea biomass as high-performance anode material for sodium-ion batteries

Hard Carbon Microsphere with Built-In Electron Transport Channels as a High-Performance Anode for Sodium-Ion Batteries

Hierarchical Porous Carbon Anode Materials Derived from Rice Husks with High Capacity and Long Cycling Stability for Sodium‐Ion Batteries

From Natural Fibers to High-Performance Anodes: Sisal Hemp Derived Hard Carbon for Na-/K-Ion Batteries and Mechanism Exploration

High-Performance Hard Carbon Anode: Tunable Local Structures and Sodium Storage Mechanism

Comparison and Optimization of Biomass-Derived Hard Carbon As Anode Materials for Sodium-Ion Batteries

A Stable Biomass‐Derived Hard Carbon Anode for High‐Performance Sodium‐Ion Full Battery

Optimizing Synthesis Temperature for Lignin-Derived Hard Carbon Anode for High Cycling Capacity in Sodium-Ion Batteries