Degradation of sulfamerazine by a novel CuxO@C composite derived from Cu-MOFs under air aeration

Yong Chen,Junfeng Zhao,Lu Hu,Jing Tian,Yong Liu

DOI: https://doi.org/10.1016/j.chemosphere.2021.130678

IF: 8.8

2021-10-01

Chemosphere

Abstract:<p>Most metal-organic frameworks (MOFs) are synthesized from carboxylate and metal precursors by hydrothermal process, which will consume a large amount of solvent and carboxylate. To address this issue, a new strategy for Cu-based MOFs was developed, in which the Cu-based MOFs was obtained by using abundant natural polymer (tannic acid) as one of the precursors and using high-energy ball milling to achieve a self-assembly of tannic acid and copper sulfate. Based on this strategy, a novel Cu-based MOFs derivative (Cu_x composite) was synthesized by high-temperature sintering of Cu-based MOFs and used for sulfamerazine (SMR) removal via O₂ activation. The BET specific surface area and average pore size of Cu_x composite were 110.34 m² g⁻¹ and 21.06 nm, respectively, which made Cu_x composite had the maximum adsorption capacity (<em>Q</em>_max) for SMR of 104.65 mg g⁻¹ and favored the subsequent degradation of SMR. The results from XRD and XPS indicated that Cu_x composite contained a lot of Cu⁰ and Cu₂O with the sizes of 76.6 nm and 9.8 nm, respectively, which led to its high performance of O₂ activation. The removal efficiency of SMR and 90.2% TOC achieved 100% and 90.2%, respectively in the Cu_x/air system at initial pH of 4.0, air flow rate of 100 mL min⁻¹, Cu_x dosage of 1 g L⁻¹ and reaction time of 30 min. Reactive species, including H₂O₂, OH and O₂^- radicals were detected in the Cu_x/air system, and OH and O₂^- were mainly responsible for the degradation of SMR.</p>

environmental sciences