Influence of Sc substitution on structure and properties of NASICON-type Na3Sc2-xRx(PO4)3 (R=Eu, Tb, Dy) phosphors

Nataliya Krutyak,Dmitry A. Spassky,Irina Kudryavtseva,Eldar M Gallyamov,Darya Filatova,Aleksandr V Mosunov,Vladimir A. Morozov

DOI: https://doi.org/10.1039/d3dt04260j

IF: 4

2024-02-08

Dalton Transactions

Abstract:Na3Sc2-xRx(PO4)3 (R=Eu, Tb, Dy; 0 ≤ x ≤ 0.2) phosphors were synthesized by a high-temperature solid-state reaction. Sc:R ratios for the NSP:xR samples were determined by ICP-MS, EDX-SEM and TEM-EDX measurements. X-ray diffraction study revealed that solid solutions with a NASICON-type structure were formed at 0 ≤ x ≤ 0.1. Luminescence properties of Na3Sc2(PO4)3 and Na3Sc2-xRx(PO4)3 (R=Eu, Tb, Dy) were studied in the range of 80–500 K. The highest R3+ luminescence intensity in Na3Sc2-xRx(PO4)3 (R=Eu, Tb, Dy) depending on R was found for x = 0.05 in the case of Dy and x = 0.1 in the case of Eu and Tb. The temperature behaviour of the R3+ emission intensity of Na3Sc2-xRx(PO4)3 (R=Eu, Tb, Dy) depends on R that replaces Sc. Decrease of the Eu3+ emission intensity depending on transition energy by ~26% and 18% at ~420 K compared to TR allows to consider the NSP:0.1Eu3+ as suitable phosphor for pc-LEDs. The temperature dependence of the Dy3+ emission for NSP:0.05Dy3+ demonstrates a strong thermal quenching. Different temperature dependence of the Tb3+ emission intensity of NSP:0.1Tb3+ was found for two excitation bands at λex = 220 and 378 nm representing f-d and f-f intracentre transitions. No thermal quenching for f-f transitions takes place while the emission intensity for f-d transitions increases with temperature rise from 80 to 500 K. The dielectric measurements for Na3Sc2(PO4)3 and Na3Sc1.9Eu0.1(PO4)3 were provided on ceramic pellets sintered under vacuum using a spark plasma sintering technique. Different dependence of conductivity was found for two samples. The calculated conductivity for Na3Sc1.9Eu0.1(PO4)3 with a R3 @#x0305;с structure σbulk = 6.4×10−5 S/cm at 300 K, 1.14×10−3 S/cm at 360 K and 5.0×10−2 S/cm at 500 K) is higher than that for pure α- Na3Sc2(PO4)3 but lower than that for β- and γ-Na3Sc2(PO4)3.

chemistry, inorganic & nuclear