Abstract:In recent years, the types and quantities of polyurethane products have increased day by day. However, traditional petroleum-based water-based polyurethanes not only have the problem of difficult waste disposal, but also accelerate the depletion of petroleum materials. Herein, an eco-friendly polymer was successfully prepared by introducing tannic acid (TA) into castor oil-based waterborne polyurethane (WPU). The effects of the incorporation of TA, a bio-based material, on the particle size of the resulting polyurethane (PU) dispersion, and the thermal performance, mechanical properties, and hydrophobicity of PU membranes were systematically investigated. Finally, ATR-FTIR and SEM of cured films after degradation were measured to characterize the degradation ability of the membranes. It was found that the tensile strength of the samples is improved from 12.67 to 19.57 MPa with the TA content increasing from 0 to 1.5%, nevertheless their elongation at break declines from 306.51 to 237.12%. A noteworthy increase in the glass transition temperature (Tg) was exhibited by using DSC and DMA for the resulting PU films with increasing the TA content. Besides, the improvement in the water absorption of the blend films decreases from 14.5 to 10.2% according to the advantage of TA increasing the degree of cross-linking of the system. After 120 days of degradation, it can be seen that the urethane bond and the aliphatic ester bond played a vital role in the degradation process through the infrared of the degraded films. At the same time, the introduction of TA improves the degradation performance of WPU films. What is more, the application of WPU dispersions containing tannins on the leather surface shows excellent comprehensive performance, which means that WPU dispersions have potential applications as leather finishing agents. This work takes advantage of two kinds of bio-based materials, the mass of bio-based materials accounts for 57% of the total mass, which not only shortens the utilization of petroleum resources, but also effectively resolved the problem that poor quality of castor oil-based WPU and traditional waste is difficult to degrade, improving the commercial value of castor oil-based PU.

A waterborne polyurethane–based leather finishing agent with excellent room temperature self-healing properties and wear-resistance

Properties of Waterborne Polyurethane Latex for Environmental Friendly Leather Finishing Agent

A rapid room-temperature self-healing, antibacterial, photoluminescent waterborne polyurethane coating with excellent mechanical properties based on double dynamic cross-linked network used for leather finishing

Polyacrylate/Prussian blue nanoparticles composite emulsion applied to photothermal self-healing leather coatings

Synthesis and self‐healing investigation of waterborne polyurethane based on reversible covalent bond

Waterborne polyurethane containing fluorosilicone coating: to endow leather with enduring hydrophobicity and mechanical properties

Mechanically robust room-temperature self-healing waterborne polyurethane with antimicrobial properties constructed through multiple dynamic bonds

Preparation of ecofriendly water-borne polyurethane elastomer with mechanical robustness and self-healable ability based on multi-dynamic interactions

Improvement for the mechanical performance of boroxine‐based self‐healing polyurethane by quadruple hydrogen bonds

Polyrotaxane‐modified waterborne polyurethane based on H‐bonding and metal bonding with mechanically tough and self‐healability

Preparation of degradable castor oil-based waterborne polyurethane with tannic acid as crosslinking agent and its application on leather surface coating

Simultaneously self-healing and photoluminescence waterborne polyurethane coatings based on dual dynamic bonds

Dipeptide end-capping resultant multiple hydrogen bonds triggering self-healing waterborne polyurethane elastomers

Self-healing and malleable waterborne polyurethane bearing aliphatic disulfide linkages with hydrophobic branching chains

Multifunctional Polyurethane Coatings with Excellent Antifouling and Self-Healing Properties

Preparation of modified CO2‐based polyurethane for wet‐type artificial leather with excellent alkali resistance

Imine-containing Self-healing Waterborne Polyurethane Elastomeric Coating Derived from Bio-based Polyester Polyol

Preparation and characterization of silicone oligomer modified polyurethane acrylates for leather finishing

Main‐Side Chain Hydrogen Bonding‐Based Self‐Healable Polyurethane with Highly Stretchable, Excellent Mechanical Properties for Self‐Healing Acid–Base Resistant Coating

Robust Self‐healing Waterborne Polyurethane Coatings Via Dynamic Covalent Diels‐Alder Bonds for Corrosion Protection

Fabrication of water-resistance and durable antimicrobial adhesion polyurethane coating containing weakly amphiphilic poly(isobornyl acrylate) Side chains