Abstract:The present work investigated the influences of the variation of Si content and the minor amount of Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys systematically. Alloy compositions with Nb-21.6(Ti/Zr)-3.1Hf-(9.4–15.6)Si-6.3Cr-3.1Al-1.0B (at. %) were designed using a cluster formula approach to realize the substitution of similar elements, in which these alloys were solid-solutionized at 1573 K for 24 h and then aged at 1273 K for 24 h. It was found that all these aged alloys are mainly composed of BCC-Nb solid solution (Nbss), Nb 5 Si 3 and Cr 2 Nb phases, where the increase of Si content and the addition of Zr could significantly increase the volume fraction of Nb 5 Si 3 in a form of coarse and primary particles. Consequently, high-Si alloys possess outstanding mechanical property at high temperature, as evidenced by the fact that the yield strength ( σ YS = 373 MPa) at 1523 K of high-Si/Zr alloy containing 15.6 at. % Si and 1.6 at. % Zr is much higher than that ( σ YS = 266 MPa) of the low-Si alloy with 9.4 at. % Si and 0 Zr. It is mainly ascribed to the existence of primary Nb 5 Si 3 particles, besides the eutectic microstructure composed of Nbss and Nb 5 Si 3 , as well as fine Cr 2 Nb precipitates in Nbss. Moreover, a minor amount of Zr substitution for the Ti is conducive to the phase transition of α-Nb 5 Si 3 to γ-Nb 5 Si 3 . Thus, this high-Si/Zr alloy exhibits an improved oxidation resistance after 50 h-exposure at 1523 K, due to the lowest mass gain of about 80.9 mg/cm 2 . The constitutions of oxide scales in these alloys were characterized and compared, from which it was found that the better oxidation resistance is closely related to the formation of dense oxide scales. This work will provide a new approach to obtain an optimum combination of mechanical property and oxidation resistance of superalloys through multi-component alloying.

On the segregation behavior and influences of minor alloying element Zr in nickel-based superalloys

Effects of Zirconium Additions on the Microstructure and Stress-Rupture Properties in Polycrystalline Ni-Based Superalloys

Effect of Zr on microstructure and hot cracking susceptibility of ZGH451 superalloy fabricated by direct energy deposition

Effect of Trace Zr on Microstructure and Hardness of Al-Zn-Mg-Cu Alloy Prepared under Supergravity

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Influences of Minor Alloying Elements on the Eutectic Volume of Ni-Base Superalloy

Micro-alloying effects of Ni on the microstructure and mechanical properties of an Al-Zn-Mg-Cu-Sc-Zr alloy

Effect of Carbon and Boron Additions on Segregation Behavior of Directionally Solidified Nickel-Base Superalloys with Rhenium

Segregation Behavior of Alloying Elements in Different Oriented Single Crystal Nickel Based Superalloys

Effects of Si variation and Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys

Effects of Re and Ru on the Solidification Characteristics of Nickel-Base Single-Crystal Superalloys

Phase Field Simulation of Alloying Element Segregation During Solidification of DD5 Nickel-Base Single Crystal Superalloy

Effect of Si on the Solidification Segregation Behavior of a New Ni–Co‐Based Superalloy

Optimizing Zr addition method to improve the comprehensive high temperature performance of Al-Fe-Ni-Sc eutectic alloy

Microstructural Instability and Precipitation Behaviors of Intermetallic Phases in a Nb-Containing CoNi-Based Superalloy

Effect of Zr Treatment on Inclusion and Solidification Microstructure in Ti Deoxidized Low Carbon Microalloyed Steel

Microstructures and Mechanical Properties of Cast Nb-Ti-Si-Zr Alloys

The effect of zirconium on the microstructure and mechanical properties of a super-high-strength Al-Zn-Mg-Cu alloy

Electronic structure of γ′ phase containing Zr In nickel-base superalloy

Effect of Zr addition on the microstructure, phase transformation and mechanical property of Ni 50 Mn 25 Ga 17 Cu 8 alloy

EFFECT OF Zr ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NiAl/Cr(Mo)BASE EUTECTIC ALLOY