A Scalable Approach to Synthesize Cobalt-Free LNMO Cathode Materials for High Energy Density Lithium Ion Batteries
Tao Hu,Yan Lin,Pekka Tynjälä,Shubo Wang,Gayathri Peta,Harishchandra Singh,Doron Aurbach,Ulla Lassi
DOI: https://doi.org/10.1149/ma2023-0283359mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:The rapid growing demand for electric vehicles (EVs) has highlighted the need for high-energy-density batteries. The cathode material plays a vital role in achieving this goal[1]. As the limitations of cathode capacity improvement are approached, the pursuit for high-voltage materials becomes a viable option[2]. Lithium nickel manganese oxide LNMO (LiNi 0.5 Mn 1.5 O 4 ) stands out due to its remarkable attributes including a substantial reversible capacity, excellent thermal stability, cost-effectiveness, environmental friendliness, and a high energy density[3]. Moreover, its cobalt-free composition aligns with sustainability objectives. Despite extensive research, the large-scale production and deployment of LNMO remain formidable challenges. In this study an industrially applicable co-precipitation method-based scalable synthesis strategy is introduced. The LNMO spheres with controlled various sizes and morphologies were successfully fabricated by adjusting the pH environment during synthesis carefully ( Fig. 1A ). Scanning electron microscopy (SEM) revealed the presence of uniformly spherical particles with dimensions of appr. 6, 9, and 14 μm and unique morphological characteristics ( Fig. 1A d-f). Synchrotron X-ray diffraction (SXRD) of LNMO samples revealed a deviation from the optimal Ni-to-Mn ratio of 1:3 ( Fig. 1B )[4,5]. This variation results from the pH-dependent metal ion precipitation dynamics during synthesis, introducing a fascinating dimension to LNMO material fabrication. As potential cathode materials for lithium-ion batteries, these samples underwent a thorough electrochemical evaluation as part of our research. Among the synthesized LNMO samples, LNMO-9 demonstrated the most promising specific capacity, surpassing approximately 138 mAh/g and working under high voltage of 4.75 V ( Fig. 1C ). Furthermore, the characterizations of the materials were also thoroughly investigated by a variety of advanced characterization techniques, including Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). This research reveals a strategy for synthesizing LNMO materials with certain regulated features and presents a successful strategy for industrial manufacturing as well. Particularly in the context of the EV industry, this research acquires critical significance in answering the growing demand for high-performance, sustainable energy storage systems. Fig. 1 (A) Illustration of the synthesis process of LNMO- x samples with SEM images of (a‒c) NiMn- x precursors and (d‒f) LNMO- x products. (B) SXRD patterns with Rietveld refinements and (C) charge/discharge profile of LNMO- x samples. Reference [1] H.-H. Ryu, G.-C. Kang, R. Ismoyojati, G.-T. Park, F. Maglia, Y.-K. Sun, Intrinsic weaknesses of Co-free Ni–Mn layered cathodes for electric vehicles, Materials Today. (2022) S1369702122000645. https://doi.org/10.1016/j.mattod.2022.03.005. [2] T. Liu, A. Dai, J. Lu, Y. Yuan, Y. Xiao, L. Yu, M. Li, J. Gim, L. Ma, J. Liu, C. Zhan, L. Li, J. Zheng, Y. Ren, T. Wu, R. Shahbazian-Yassar, J. Wen, F. Pan, K. Amine, Correlation between manganese dissolution and dynamic phase stability in spinel-based lithium-ion battery, Nat Commun. 10 (2019) 4721. https://doi.org/10.1038/s41467-019-12626-3. [3] Y. Xue, L.-L. Zheng, J. Wang, J.-G. Zhou, F.-D. Yu, G.-J. Zhou, Z.-B. Wang, Improving Electrochemical Performance of High-Voltage Spinel LiNi 0.5 Mn 1.5 O 4 Cathode by Cobalt Surface Modification, ACS Appl. Energy Mater. 2 (2019) 2982–2989. https://doi.org/10.1021/acsaem.9b00564. [4] A. Gomez, G. Dina, S. Kycia, The high-energy x-ray diffraction and scattering beamline at the Canadian Light Source, Review of Scientific Instruments. 89 (2018) 063301. https://doi.org/10.1063/1.5017613. [5] H.M. Rietveld, A profile refinement method for nuclear and magnetic structures, J Appl Crystallogr. 2 (1969) 65–71. https://doi.org/10.1107/S0021889869006558. Figure 1