Optimization of Process Parameters for Bamboo Fiber Extraction by Steam Explosion

Wenjuan Zhao,Yanping Zou,Wenfu Zhang,Hong Chen,Jian Zhang,Anqi Wu,Shaofei Yuan,Ying Zhao

DOI: https://doi.org/10.1080/15440478.2023.2301369

2024-01-21

Journal of Natural Fibers

Abstract:Bamboo fiber (BF) has emerged as a promising natural, environmentally friendly material for use in composite materials. The steam explosion process plays a crucial role in preparing BFs suitable for composites. In this study, the effects of solid–liquid ratio, explosion pressure, and explosion holding time on BF preparation were investigated by orthogonal experiments, and the structural and chemical changes occurring during the separation of BF were also investigated. The results showed that the combined method of alkali treatment and steam explosion successfully produced BFs with good morphology. The highest yield of fine fibers (39.07%) was obtained at a solid–liquid ratio of 2:1, explosion pressure of 2.2 MPa, and explosion holding time of 4 min. BFs obtained using the optimal values exhibited dispersed fiber bundles, partial removal of hemicellulose and lignin, and improved crystallinity. Furthermore, the hygroscopicity of BFs decreased, reaching a minimum of 15% under the optimal process conditions. The optimization of steam explosion parameters can help to improve the extraction efficiency of fine fibers for composites and promote the industrialization of BFs prepared by steam explosion. 竹纤维(BF)已成为复合材料领域中一种前景广阔的天然环保材料. 蒸汽爆破工艺在制备适用于复合材料的BFs中起着至关重要的作用. 本研究采用正交实验研究了固液比、爆破压力和保压时间对BF制备的影响,并研究了BF分离过程中发生的结构和化学变化. 结果表明,碱处理和蒸汽爆破相结合的方法成功地生产出了形态良好的BF. 在固液比为2:1、爆破压力为2.2 MPa、爆破保压时间为4 min的条件下,细纤维的产率最高(39.07%). 使用最佳值获得的BFs为分散的纤维束,部分去除半纤维素和木质素并提高了结晶度. 此外,在最佳工艺条件下,BFs的吸湿性降低,最低可达15%. 蒸汽爆破参数的优化有助于提高适用于复合材料的细纤维的提取效率,促进蒸汽爆破法制备BFs的工业化.

materials science, textiles

What problem does this paper attempt to address?

The paper mainly discusses the optimization of process parameters in the extraction of bamboo fiber (BF) through the steam explosion method. The aim of the study is to improve the extraction efficiency of bamboo fiber and enhance fiber quality, thereby promoting the industrial application of bamboo fiber.

Specifically, the study investigates the effects of factors such as solid-liquid ratio, explosion pressure, and holding time on bamboo fiber extraction through orthogonal experimental methods. The experimental results show that the optimal extraction conditions are a solid-liquid ratio of 2:1, explosion pressure of 2.2 MPa, and holding time of 4 minutes. Under these conditions, a maximum fine fiber yield of up to 39.07% can be obtained.

In addition, the study found that bamboo fibers treated under optimal conditions exhibit good morphological characteristics, including dispersed fiber bundles, partial removal of hemicellulose and lignin, and increased crystallinity. Meanwhile, the hygroscopicity of bamboo fiber is also reduced, with the lowest being reduced to 15%.

In summary, this study aims to improve the extraction efficiency and quality of bamboo fiber by optimizing the steam explosion process parameters, providing theoretical and technical support for the industrial application of bamboo fiber in the field of composite materials.