Abstract:This study repots the preparation of porous zinc nanosheets using the hydrogen bubble template method. The obtain results demonstrate a high Faradaic efficiency of 89.5 % and a partial current density of −6.2 mA/cm2 at moderate potential. Additionally, the prepared catalysis shows exceptional stability for over 10 h. With the increasing levels of CO2 emissions and the decreasing availability of energy resources, the electrocatalytic CO2 reduction reaction (CO2RR) offers a promising method for utilizing CO2 as a valuable resource using sustainable electrical energy. However, developing cost‐effective and highly efficient catalysts remains a significant challenge. Although zinc, an abundant element on Earth, has shown potential for converting CO2 into CO, its effectiveness as a catalyst for CO2 reduction is hindered by its low selectivity and stability. This study introduces a fast, efficient, and simple electrochemical deposition method for preparing porous zinc nanosheets (NS) using the hydrogen bubble template approach. The as‐prepared zinc NS catalyst demonstrates exceptional catalytic activity due to its highly porous structure and high specific surface area. At a voltage of −1 V versus RHE, it achieves a maximum CO Faradaic efficiency of 89.5 %. The performance of this system is characterized by a partial current density of around −6.17 mA cm−2 in an H‐cell configuration. Additionally, our catalyst exhibits remarkable durability over 10 h, highlighting its significant potential for real‐world utilization in CO2RR.

Highly efficient zinc electrode prepared by electro-deposition in a salt-induced pre-phase separation region solution

Rational Design and Synergistic Effect of Ultrafine Ag Nanodots Decorated Fish-Scale-like Zn Nanoleaves for Highly Selective Electrochemical CO2 Reduction

Three-Phase-Heterojunction Cu/Cu2O-Sb2O3 Catalyst Enables Efficient CO2 Electroreduction to CO and High-Performance Aqueous Zn-CO2 Battery

Zn electrode with a layer of nanoparticles for selective electroreduction of CO2 to formate in aqueous solutions

Local Environment-Mediated Efficient Electrocatalysis of CO2 to CO on Zn Nanosheets

Atomically Defined Undercoordinated Active Sites for Highly Efficient CO2 Electroreduction

Efficient CO 2 electroreduction to CO at low overpotentials using a surface-reconstructed and N-coordinated Zn electrocatalyst.

One‐step Synthesis of Ultra‐small Amount of Pd‐Alloyed Zinc Nanosheets for Efficient Electrochemical CO2 Reduction to CO

Boosting CO production in electrocatalytic CO2 reduction on highly porous Zn catalysts

One‐step synthesis of ultra‐small amount of Pt‐Alloyed Zinc Nanosheets for efficient electrochemical CO2 reduction to CO

Boosting CO<sub>2</sub> electroreduction on a Zn electrode <i>via</i> concurrent surface reconstruction and interfacial surfactant modification

Electrodeposited Zn Dendrites with Enhanced CO Selectivity for Electrocatalytic CO2 Reduction

A Highly Efficient Zinc Catalyst for Selective Electroreduction of Carbon Dioxide in Aqueous Nacl Solution

Facile Synthesis of Porous Zinc Nanosheets for Highly Selective Electrochemical CO2 Reduction to CO

Exfoliated Ultrathin ZnIn2S4 Nanosheets with Abundant Zinc Vacancies for Enhanced CO2 Electroreduction to Formate

Three-dimension Porous Zn-Cu Alloy: an Inexpensive Electrocatalyst for Highly Selective CO2 Reduction to CO in Non-Aqueous Electrolyte

Electrochemical Reduction of CO2 to CO on Hydrophobic Zn Foam Rod in a Microchannel Electrochemical Reactor

Three-dimension porous Zn-Cu alloy: An inexpensive electrocatalyst for highly selective CO 2 reduction to CO in non-aqueous electrolyte

Fabrication of ZnO nanosheets self-assembled by nanoparticles for accelerated electrocatalytic reduction of CO2 to CO

Two-step facile synthesis of Co3O4@C reinforced PbO2 coated electrode to promote efficient oxygen evolution reaction for zinc electrowinning

CO2-Induced Fibrous Zn Catalyst Promotes Electrochemical Reduction of CO2 to CO