Seismic performance of large rupture strain FRP retrofitted RC columns with corroded steel reinforcement
Yingwu Zhou,Xuan Chen,Xiaohan Wang,Lili Sui,Xiaoxu Huang,Menghuan Guo,Biao Hu
DOI: https://doi.org/10.1016/j.engstruct.2020.110744
IF: 5.582
2020-08-01
Engineering Structures
Abstract:Retrofitting reinforced concrete (RC) column by conventional fibre reinforced polymers (FRPs) can enhance the seismic performance to a limited level due to the small straining capacity and brittle failure of FRP. Existing findings have substantiated that the polyethylene terephthalate (PET) FRP with large rupture strain (LRS) (e.g., greater than 5%) are regarded as preferable to conventional FRP concerning enhancing the ductility of retrofitted RC columns. This paper experimentally evaluates the enhancement in seismic performance of corroded RC columns contributed by LRS-FRP strengthening based on testing of ten RC columns. The main test variables are the corrosion ratio of longitudinal reinforcement, axial force ratio, thickness of LRS-FRP and boundary condition. The seismic performance is systematically evaluated, including crack pattern, failure mode, lateral load resistance, hysteretic response, energy-dissipation capacity, stiffness degradation, ductility and strain responses of wrapped LRS-FRP. The results indicate that corrosion results in significant performance degradation in member strength and ductility. Notably, the failure mode of un-retrofitted corroded columns changes from typical flexural failure to shear-compression failure when the axial load ratio increases from 0.2 to 0.4, which case is prevented by LRS-FRP strengthening so that the retrofitted corroded column eventually experiences ductile flexural failure under larger axial load ratio. Moreover, LRS-FRP retrofitting remarkably improves the ductility and energy dissipation capacity of corroded RC columns compared with the un-retrofitted counterparts.