Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

Fracture toughness of AlTiN coatings investigated by nanoindentation and microcantilever bending

Mechanical Properties and Fracture Toughness of Multilayer Hard Coatings Using Nanoindentation

Toughness measurement of thin films based on circumferential cracks induced at conical indentation

Mechanical Performance of AlCrSiN and AlTiSiN Coatings on Inconel and Steel Substrates after Thermal Treatments

Investigating the structure, adhesion and tribological properties of Al and Zr-doped TiN coatings with various substrate bias voltage and working pressure

In situ micro-cantilever tests to study fracture properties of NiAl single crystals

Study of mechanical behavior, deformation, and fracture of nano-multilayer coatings during microindentation and scratch test

Microstructure effects on fracture failure mechanism of CrAl/CrAlN coating

The effect of coating cracking on the indentation response of thin hard-coated systems

Evaluation of wear resistance of CrN, CrAlN, and TiAlN coatings deposited by multi-arc ion plating on spinning die of Cr12MoV

The Effect of Al and Ti Transition Metals on the Wear Resistance of Ceramic Based CrN Coatings; Investigation under Ambient Air and Vacuum Conditions

Tribological behaviour of TiAlN and AlCrN coatings on stainless steel

Hard Yet Tough Thermodynamics-Driven Nanostructured (alcrnbsixti)n Multicomponent Nitride Hard Coating

Mechanical, Tribological, and Corrosion Resistance Properties of (TiAlxCrNbY)Ny High-Entropy Coatings Synthesized Through Hybrid Reactive Magnetron Sputtering

Tribological Properties of Craln and Tin Coatings Tested in Nano- and Micro-Scale Laboratory Wear Tests

Nitriding Effect on the Tribological Performance of CrN-, AlTiN-, and CrN/AlTiN-Coated DIN 1.2367 Hot Work Tool Steel

Comparative investigation and characterization of the nano-mechanical and tribological behavior of RF magnetron sputtered TiN, CrN, and TiB2 coating on Ti6Al4V alloy

Fabrication and Performance of TiN/TiAlN Nanometer Modulated Coatings

A comparative study of hardness/scratch/wear properties of TiCN and TiAlN coatings on DIN 1.2842 steel by CA-PVD method

Growth, mechanical properties, and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

Properties and Performance of TiAlSiN and AlCrN Monolayer and Multilayer Coatings for Turning Ti-6Al-4V