Understanding reactions between water and steelmaking slags: Iron distribution, hydrogen generation, and phase transformations
Peng Li,Xiangyang Li,Hongwei Guo,Bingji Yan,Dong Chen,Wei Zhao,Seshadri Seetharaman
DOI: https://doi.org/10.1016/j.ijhydene.2022.04.209
IF: 7.2
2022-05-16
International Journal of Hydrogen Energy
Abstract:Environmentally friendly energy harvesting can be achieved by the H 2 O thermochemical treatment of steelmaking slags. Hot slag from steel manufacturing is used as a sacrificial material to produce H 2 in a stream of steam. In parallel, this process enhances the magnetic properties of the slag, benefitting the Fe recovery. In this work, the occurrence states of different iron species in slags, as well as their reactivity and phase transformations in H 2 O, were investigated. The results showed that Fe 2+ was mainly distributed in olivine (Ca, Fe, Mg, Mn) 2 SiO 4 when the basicity was low. As the basicity increased, a gradual enrichment of Fe 2+ in RO phase (divalent oxides solid solution, R = Fe, Mg, Mn etc.) was observed. In addition to steelmaking slags, the H 2 O splitting reactions of synthetic model iron compounds, RO phase (Mg 1–x Fe x O, x = 0.36, 0.63, 0.77) and kirschsteinite (CaFeSiO 4 ) were also tested. RO phase exhibited fast kinetics, with its activity proportional to the FeO content. Oxidation of the magnesia-rich RO phase resulted in the phase segregation of iron-depleted magnesiowüstite (Mg,Fe depleted )O and iron-rich spinel (Mg,Fe rich ) 3 O 4 . The H 2 O splitting of CaFeSiO 4 suffered from extremely low kinetics below 900 °C, which could be enhanced by raising the temperature. The H 2 production capacity of steelmaking slags was strongly affected by the basicity, which improved when more Fe 2+ existed as RO phase rather than CaFeSiO 4 . After oxidation in steam at 850 °C, the slag sample with a basicity of 1.83 produced 29.3 cm 3 ⋅g −1 material hydrogen at 850 °C for 60 min, with a conversion ratio of 80.1%.
energy & fuels,electrochemistry,chemistry, physical