Structure, performance, morphology and component transformation mechanism of LiMn0·8Fe0·2PO4/C nanocrystal with excellent stability

Ting Luo,Tao-tao Zeng,Shi-lin Chen,Rong Li,Run-zhen Fan,Han Chen,Shao-chang Han,Chang-ling Fan
DOI: https://doi.org/10.1016/j.jallcom.2020.155143
IF: 6.2
2020-09-01
Journal of Alloys and Compounds
Abstract:LiMn0·8Fe0·2PO4/C nanocrystal was synthesized by a facile solvothermal reaction. The pH and concentration of lithium ion are changing with the increase of LiOH. The deposition law of precursor ions is investigated, in which Li+ exceeds the necessary stoichiometric ratio even in the lowest amount of LiOH. Mn2+ and Fe2+ possess the similar fixation tendency, and 87.88% Mn2+ are deposited at the pH of 3.30. However, nearly all Fe2+ are precipitated in a wide pH range (2.96–3.85). The morphology changes from nanosheet to nanoellipsoid under the cooperation of pH and precursor ions. The components of LiMnPO4 and LiFePO4 in LiMn0·8Fe0·2PO4/C are predicted and their contributions to capacity are close to the actual results. Sample S-2.6 delivers the optimum electrochemical performance with a capacity of 150.9, 134.6 and 107.5 mA h·g−1 at 0.05, 1 and 5 C, respectively. It also exhibits high reversibility, low charge transfer resistance (41.2 Ω) and excellent diffusion coefficient (5.38 × 10−11 cm2·s−1). The capacity retention of sample S-2.6 reaches 96.03% after 200 cycles and it maintains original structure without obvious change according to the ex-situ XRD results. The morphology of the cycled cathode film also maintains its integrity without evident cracks. The low dissolution of Mn2+ and Fe2+ from LiMn0·8Fe0·2PO4/C shows the enhanced chemical stability.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper primarily explores the synthesis of lithium manganese iron phosphate (LiMn\_0.8Fe\_0.2PO4/C) nanocrystal materials through the solvothermal method and investigates the effects of different lithium hydroxide (LiOH) molar ratios on the material's structure, performance, and morphology. ### Main Research Questions: 1. **Investigate the impact of LiOH molar ratio changes on the synthesis of LiMn\_0.8Fe\_0.2PO4/C nanocrystal materials**: - Study how the LiOH molar ratio affects the pH value of the reaction system, thereby influencing the material's morphology, structure, and composition. - Explore the impact of LiOH molar ratio on the material's electronic conductivity, surface area, and porosity. 2. **Optimize the electrochemical performance of LiMn\_0.8Fe\_0.2PO4/C materials**: - Optimize the material's morphology by adjusting the LiOH molar ratio to improve its electrochemical performance, including charge-discharge capacity, rate performance, and cycling stability. - Study the charge-discharge characteristics of the material at different current densities and analyze its electrochemical impedance spectroscopy. 3. **Understand the relationship between material structure and electrochemical performance**: - Analyze the proportions of different components (such as LiMnPO4, LiFePO4, etc.) in LiMn\_0.8Fe\_0.2PO4/C materials and their contributions to electrochemical performance. - Investigate the chemical stability of the material, including the dissolution behavior of manganese ions and iron ions from the material. ### Key Findings: - It was found that changes in the LiOH molar ratio can significantly affect the material's morphology, transforming from nanosheet to nano-ellipsoid. - An optimal LiOH molar ratio (2.6) was identified, under which the synthesized material exhibits the best electrochemical performance, including high capacity retention, low charge transfer resistance, and excellent lithium-ion diffusion coefficient. - The material demonstrated good cycling stability and structural stability, maintaining a high capacity retention rate after 200 cycles, with no significant changes in material structure. - The dissolution behavior of manganese ions and iron ions in the electrolyte was studied, indicating that the material has enhanced chemical stability. In summary, this study aims to achieve effective control over the morphology and performance of LiMn\_0.8Fe\_0.2PO4/C nanocrystal materials by finely tuning the LiOH molar ratio, in order to obtain new lithium-ion battery cathode materials with excellent electrochemical performance.