Abstract:The truncated octahedral LiNi0.08Mn1.92O4 (LNMO) cathode material with dominant {111}, truncated {110} and {100} crystal planes was prepared by a low temperature solid-state combustion method. The dominant {111} crystal plane of the unique truncated octahedron can form firm solid electrolyte interphase (SEI) layer and alleviate the manganese dissolution during the discharge-charge process, and a small part of {110} and {100} crystal planes can increase the rapid diffusion channels of Li+ ions. The field emission scanning electron microscope (SEM) and X-ray diffractometer (XRD) results show that LNMO has cubic spinel structure with submicron particle size. The electrochemical performances of LNMO are also outstanding at high temperature of 55 degrees C, the initial discharge capacities are 109.9 and 98.0 mAh/g with capacity retentions of 75.8% and 80.5% after 300 cycles at 1 and 5 C, respectively. Even at high current rates of 10 and 15 C, the capacity retentions of 48.4% and 49.4% have been maintained after 1000 cycles, while the capacity loss of undoped LiMn2O4 is as high as 98% after 1000 cycles at 15 C. Moreover, the dynamic performance tests show that LNMO owns larger Li+ diffusion coefficient (D=3.86x10(-15) cm(2)/s), smaller charge transfer resistances (before cycle and after cycles, the R-ct=158.0 and 279.8 Omega) and lower apparent activation energy (E-a=17.63 kJ/mol) than LiMn2O4 (LMO), demostrate its enhanced Li+ transport dynamic. The XRD tests of two electrode slices after 1000 cycles at 10 C show that the crystal structure of LNMO electrode material is almost unchanged, which indicated that the Ni doping and the truncated octahedral structure of particles could improve the structural stability of material, effectively inhibit the Jahn-Teller effect and Mn dissolution, remarkably improve its high temperature electrochemical performance. Therefore, this work provides a reference for the application of spinel LiMn2O4 electrode material at high temperature.

Submicron single-crystalline LiNi0.5Mn1.5O4 cathode with modulated Mn3+ content enabling high capacity and fast lithium-ion kinetics

Improved Li-ion Diffusion and Stability of a LiNi0.5Mn1.5O4 Cathode Through in Situ Co-Doping with Dual-Metal Cations and Incorporation of a Superionic Conductor

Optimized Morphology and Tuning the Mn3+ Content of LiNi0.5Mn1.5O4 Cathode Material for Li-Ion Batteries

Preparation and High Temperature Electrochemical Performance of LiNi0.08Mn1.92O4 Cathode Material of Submicron Truncated Octahedron

Addressing Mn Dissolution in High‐Voltage LiNi0.5Mn1.5O4 Cathodes via Interface Phase Modulation

Sr–Y co-doped LiNi0.5Mn1.5O4 cathode material with modified crystal and improved electrochemical performance

Increased Capacity of LiNi1/3Co1/3Mn1/3O2–Li[Li1/3Mn2/3]O2 Cathodes by MnOx‐surface Modification for Lithium‐Ion Batteries

Electrochemical Characterization of Ni-F Co-doped Nano LiMn2O4 Cathode Materials

Suppressed Phase Separation in High-Voltage LiNi0.5Mn1.5O4 Cathode Via Co-doping

Overlithiation-driven structural regulation of lithium nickel manganese oxide for high-performance battery cathode

Enhanced Electrochemical Performance of the Lithium-Manganese-Rich Cathode for Li-Ion Batteries with Na and F CoDoping

Ni/Mn ratio and morphology-dependent crystallographic facet structure and electrochemical properties of the high-voltage spinel LiNi0.5Mn1.5O4 cathode material

Improving Fast-Charging Capability of High-Voltage Spinel LiNi0.5Mn1.5O4 Cathode under Long-Term Cyclability Through Co-Doping Strategy

Improved long cycle performance of LiMn<sub>2</sub>O<sub>4</sub> cathode material by Ni-B co-doping combined with truncated octahedron morphology

Molybdenum-doped Lithium-Rich Layered-Structured Cathode Material Li1.2Ni0.2Mn0.6O2 with High Specific Capacity and Improved Rate Performance

Improved Electrochemical Performance of Spinel LiNi0.5Mn1.5O4 Cathode Materials with a Dual Structure Triggered by LiF at Low Calcination Temperature

Enhanced electrochemical performances of single crystal layered LiNi0.5Mn0.5O2 cathode through Na doping

Improved Capacity Retention and Ultralong Cycle Performance of Ni-Fe Co-Doped LiMn2O4 Cathode Material at High Current Densities

Granularity control enables high stability and elevated-temperature properties of micron-sized single-crystal LiNi0.5Mn1.5O4 cathodes at high voltage

Syntheses and electrochemical properties of the Na-doped LiNi 0.5 Mn 1.5 O 4 cathode materials for lithium-ion batteries

Ni, Mo Co-doped Lithium Manganate with Significantly Enhanced Discharge Capacity and Cycling Stability