Co 8 FeS 8 /N,S-Doped Carbons Derived from Fe-Co/S-Bridged Polyphthalocyanine: Efficient Dual-Function Air-Electrode Catalysts for Rechargeable Zn-Air Batteries
Lu Chen,Li−Li Cui,Zizhun Wang,Xingquan He,Wei Zhang,Tewodros Asefa
DOI: https://doi.org/10.1021/acssuschemeng.0c00124
2020-08-07
Abstract:Efficient, durable, nonprecious metal-based catalysts for electrochemical reactions involving oxygen are needed to advance the widespread use of fuel cells and Zn-air batteries. In this work, hybrid materials composed of bimetallic (Co and Fe) sulfide (Co<sub>8</sub>FeS<sub>8</sub>) nanoparticles supported on N,S-doped carbon microparticles that can serve as dual-function oxygen electrocatalysts are synthesized. The synthesis of the materials is performed by preparing and then pyrolyzing silica-protected Fe- and Co-modified, S-containing polyphthalocyanine at different temperatures. The materials are named (Fe,Co)SPPc-<i>T</i>-sp, where <i>T</i> denotes the pyrolysis temperature and sp represents the silica protection applied for their synthesis. Among them, the material synthesized at 900 °C, denoted (Fe,Co)SPPc-900-sp, shows superb electrocatalytic activities in an alkaline solution both toward the oxygen reduction reaction (ORR), with a half-wave potential (<i>E</i><sub>1/2</sub>) of 0.830 V vs RHE, and toward the oxygen evolution reaction (OER), with a current density of 10 mA cm<sup>–2</sup> at an overpotential (η<sub>10</sub>) of 353 mV. The catalytic activities of this material for both reactions are comparable with those of the respective benchmark, precious-metal-based catalysts, namely, Pt/C (20 wt %) and RuO<sub>2</sub>, respectively. An alkaline Zn-air battery assembled using (Fe,Co)SPPc-900-sp as an air electrode delivers a high peak power density (158.6 mW cm<sup>–2</sup>) and outstanding charge–discharge cycling stability (for over 50 h). These catalytic performances are better than those of the corresponding battery containing Pt/C and RuO<sub>2</sub> electrocatalysts. This work also offers a facile synthetic strategy for the fabrication of robust, inexpensive dual-function electrocatalysts for Zn-air batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c00124?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c00124</a>.Characterization results, spectra, and tables containing data (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c00124/suppl_file/sc0c00124_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology