Abstract:In this work, a polymer precursor was first synthesized using p-terphenyl (TP) and terephthaloyl chloride (TC) as monomers. Then, cross-linking was realized by means of a Schiff base reaction with melamine (MA) as a modifier to obtain an amine-functionalized porous organic polymer TP-TC-MA. The synthesized polymers were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), and point of zero charge (pHpzc) measurements, as well as on the basis of nitrogen adsorption-desorption isotherms. Adsorption experiments were carried out to evaluate the adsorption properties of TP-TC-MA for methyl orange (MO), a typical anionic azo dye that has widespread industrial application. The amount of MO adsorbed on TP-TC-MA was evaluated by ultraviolet-visible (UV-Vis) spectroscopy at a wavelength of 463 nm. Microscopic analysis revealed that the as-synthesized polymer had an aggregated particle-shaped structure. XRD spectra confirmed that TP-TC-MA was an amorphous polymer, consistent with the results of high-resolution TEM experiments. The Brunauer-Emmett-Teller (BET) specific surface area and total pore volume of TP-TC-MA were determined as 708.5 m 2/g and 0.556 cm3/g, respectively. The measured pHpzc of TP-TC-MA was 4.0, probably because of the abundant nitrogen-containing groups provided by MA. The factors affecting adsorption, such as pH, adsorbent dosage, contact time, initial pollutant concentration, and ionic strength, were investigated. Because of the protonation of the N-atom in TP-TC-MA, the pH had a strong impact on the adsorption of MO. The removal efficiency could be maximized at the optimized pH of 3.0. The adsorption equilibrium isotherm, measured at 25 ℃ and a concentration of 50-500 mg/L, showed that the MO adsorption over TP-TC-MA followed the Langmuir isotherm, with a maximum adsorption capacity of 156.3 mg/g. The modeling of the experimental adsorption data was consistent with the pseudo-second-order kinetic model, which indicated fast adsorption and chemisorption as the dominant mechanism. With increasing ionic strength, the adsorption of MO slightly decreased, suggesting a partial antagonistic ion effect. Results of the selectivity study revealed that TP-TC-MA was more selective toward MO than methylene blue (MB), which indicated that electrostatic interactions played a significant role during the adsorption progress. Five adsorption-desorption cycles showed that TP-TC-MA could be regenerated without significant deterioration of its adsorption efficiency, indicating that it has good stability and reusability. The observed adsorption performance indicated that this MA-modified porous organic polymer offers prospects for further research and application in the treatment of dye-containing wastewaters.

MOFs bound to melamine sponge for dye removal

Synthesis of magnetic metal-organic framework (MOF) for efficient removal of organic dyes from water

Water-stable methyl-modified MOF and mixed matrix membrane for efficient adsorption and separation of cationic dyes

[Preparation of melamine-functionalized porous organic polymer and its adsorption properties for methyl orange]

Bio-based adsorption foam composed of MOF and polyethyleneimine-modified cellulose for selective anionic dye removal

Lignin-modified metal–organic framework as an effective adsorbent for the removal of methyl orange

Insights into High-Performance and Selective Elimination of Cationic Dye from Multicomponent Systems by Using Fe-Based Metal–Organic Frameworks

Removal performance and adsorption kinetics of dyes by a Co-based metal organic framework

Selective Separation of Methyl Orange from Water Using Magnetic ZIF-67 Composites

Designed Construction of 2D Honeycomb Cationic MOF Materials for Selective Removal of Sulfonic Anionic Dyes

Waste organic dye removal using MOF-based electrospun nanofibers of high amine density

Magnetic Metal–Organic Framework (Fe3O4@MIL-101) Functionalized with Dendrimer: Highly Efficient and Selective Adsorption Removal of Organic Dyes

Adsorption of Methyl Orange Dyes on Oriented Co/Fe-MOF Bimetallic Organic Framework in Wastewater Treatment

Photocatalytic MOF fibrous membranes for cyclic adsorption and degradation of dyes

Performance of defective Zr-MOFs for the adsorption of anionic dyes

Recent Advances in MOF-Based Adsorbents for Dye Removal from the Aquatic Environment

Ternary Metal Oxide Embedded Carbon Derived from Metal Organic Frameworks for Adsorption of Methylene Blue and Acid Red 73.

In situ growth of Zr-based metal-organic frameworks on cellulose sponges for Hg 2+ and methylene blue removal

Metal-organic Gel Templated Synthesis of Magnetic Porous Carbon for Highly Efficient Removal of Organic Dyes.

In Situ Electrospun Porous MIL-88A/PAN Nanofibrous Membranes for Efficient Removal of Organic Dyes

Electrostatically Spun Fabrication of Fe3O4@SiO2/PVA Membranes for Efficient Methyl Orange (MO) Adsorption and Response Surface Optimization of the Processes