A green method for solidification and recovery of soluble sodium in red mud via super-gravity
Jintao Gao,Xintuo Qu,Xi Lan,Yu Li,Zhancheng Guo
DOI: https://doi.org/10.1016/j.psep.2022.03.059
IF: 7.8
2022-05-01
Process Safety and Environmental Protection
Abstract:Red mud produced in the Bayer process is an ultrafine solid waste containing various metallic elements, which is hazardous to the environment because of its high alkalinity caused by the soluble sodium (Na). In this study, a green method for efficiently solidification and recovery of soluble sodium to eliminate high alkalinity of red mud via super-gravity was developed. Iron-slag melting separation from red mud was firstly conducted at 1523 K, where the Fe was fully recovered into metallic iron and almost all the Na was enriched into the Na-rich slag. Subsequently, the Na was selectively solidified into a stable phase of anorthite at 1373–1323 K, all of which were efficiently separated from the Na-rich slag at 1323 K via super-gravity, where the recovery ratio of Na in anorthite was up to 97.09%. Compared to the red mud, the leaching rates of Na+ in the anorthite and residue were significantly decreased to 0.01% and 0.05%, and the pH of both products was decreased to 8.1–8.4. It was confirmed that the high soluble sodium in red mud was efficiently solidified and recovered into a stable phase of anorthite, and the high alkalinity was fully eliminated in both products which are environmentally friendly.Red mud is one kind of by-products rejected from industrial production of alumina plant and characterized by high content of alkaline and containing many valuable metals such as iron, aluminum, titanium, etc. It is urgent to effectively utilize red mud for the sustainable development of aluminum metallurgy industry. In this paper, a new route was proposed to fully recover Fe, Al2O3 and TiO2 from the red mud, which includes three procedures, i.e. pre-reducing-smelting, alkaline leaching and acid leaching. The pre-reducing-smelting step was employed to recover iron from the mud, producing pig iron at an iron recovery of some 98.15% and slag containing 43.17%Al2O3 and 15.71%TiO2, respectively. Then, based on the thermal dynamic calculations, a modification of the slag-alkaline leaching and hydrochloric acid leaching process were conducted to obtain the stepwise recovery of Al2O3 and TiO2, respectively, from the smelting slag. Aluminum and titanium were recovered in the form of sodium aluminum solution and perovskite at a recovery of 85.85% and 95.53%, respectively. The innovative route is probably a potential way to achieve comprehensive and clean utilization of red mud.Bauxite residue is an alkaline solid waste produced during the extraction of alumina from bauxite, which causes serious environmental problems and safety risks. In this study, alkali and alumina were recovered from Bayer bauxite residue using a novel calcification-carbonisation process. This produced a non-hazardous and near-neutral residue (C-C residue), the properties of which facilitated its subsequent reuse. After the calcification-carbonisation treatment, 46.5% of the alumina was extracted and the Na2O content in the final residue (C-C residue) dropped to less than 0.3%. In addition, the feasibility of using C-C residue in the production of cement and the preparation of soil was analysed. The results showed that the chemical composition of C-C residue is very close to that of Portland cement clinker, which allows the dosage of bauxite residue in cement production to be increased. A comparison of the C-C residue with a general soil showed that the former performed well for many soil parameters, such as alkalinity and salinity, and has great potential for application in soil preparation. Thus, the calcification-carbonisation method, combined with cement production or soil preparation, is a sustainable process for completely reusing Bayer bauxite residue and facilitating bauxite waste minimisation.A novel process for recovery of aluminum, iron, vanadium, scandium, titanium and silicon from red mud was proposed. The parameters of HCl leaching, solvent extraction, polymerization process, alkali leaching with pressure, and aging process were investigated. The results show that more than 96 % of scandium and vanadium could be leached by using HCl with many aluminum, iron and few titanium and silicon from red mud. More than 97 % of vanadium and scandium was extracted by solvent extraction with mono(2-cthylhexyl)2-cthylhexyl phosphonate (P507), but few other elements from the acid leaching solution. The rich vanadium liquid and rich scandium liquid could be obtained by washing the saturated organic phase. More than 97 % of iron and aluminum could be precipitated as the polyaluminum ferric chloride from the raffinate. The rich titanium material of TiO2 with grade of 62 % was obtained by NaOH leaching with pressure from the acid leaching residue. The white carbon black with purity of 99.5 % was obtained by -Abstract Truncated-
engineering, environmental, chemical