N/S Co-Modified Carbon/Na3V2(PO4)3 with High Rate Capability in Zn-ion storage

Yongqing Liang,Shaolong Xu,Chenxia Zhang,Zheng Liu,Pintian Zou,Bin Huang,XinChao Lu,Yi-ju Lv

DOI: https://doi.org/10.1039/d2nj06264j

IF: 3.3

2023-02-15

New Journal of Chemistry

Abstract:Na3V2(PO4)3 (NVP) with NASICON structure serves as one of the most promising cathode materials for aqueous zinc-ion batteries (AZIBs) due to its stable crystal structure and fast ion mobility. Nevertheless, the electrochemical properties are still unsatisfactory because of its poor electrical conductivity. A simple hydrothermal method is used to prepare carbon-coated NVP (NVP-C) and N/S co-doped carbon-coated NVP (NVP-C-NS). Results demonstrate that NVP-C-NS composite exhibit superior capacity and rate capability. After 100 cycles at a high current density of 1000 mA g-1, the reversible capacity of NVP-C-NS composite can achieve 115 mAh·g-1, while pure NVP-C is only capable of 83 mAh·g -1 at the same current density, and 94.8% of the capacity of the NVP-C-NS composite and only 90% for the NVP-C material are retained. The excellent electrochemical performance of NVP-C-NS composite is mainly due to the high carbon content (13.08 wt% vs. NVP-C with 4.8 wt%.) and high conductivity (3.72×10-4 S cm-1 vs. NVP-C with1.20×10-4 S cm-1). The introduction of more active sites and defects after N/S doping and the increased specific surface area can provide a larger electrochemical contact surface for electrochemical reactions. Furthermore, the practicality of the NVP-C-NS//Zn battery is evaluated by lighting up LED bulbs. This work provides a reference for the development of Na3V2(PO4)3 as a cathode material for AZIBs.

chemistry, multidisciplinary