Hot Tear Formation during the Casting of Al‐Zn Binary Alloys
Bing Yang,Jianchun Wu,Yu Zeng,Jinyan Liu,Nan Yang,Damian McGuckin,Allen Chhor,David StJohn,Matthew Dargusch,Gui Wang
DOI: https://doi.org/10.1002/adem.202301471
IF: 3.6
2023-11-25
Advanced Engineering Materials
Abstract:The hot tearing susceptibility of Al‐Zn binary alloys with solute contents of Al‐0.5%Zn, Al‐1%Zn, Al‐2%Zn and Al‐4%Zn, with all compositions being in wt%, has been investigated through physical experiments and numerical simulation. The temperature at the hot spot, the designed critical point for hot tearing, and the load at the end of the test bar have been measured and compared with the simulation results. The test samples with 0.5 and 1.0% Zn showed hot tears while those with 2.0 and 4.0% Zn had no sign of such tearing. The evolution of the solid fraction, strain, stress and hot tearing indicator have been investigated in detail to reveal the correlation between them using the simulation results. A comparison has been made between the Al‐1%Zn and Al‐4%Zn alloys. In the last moments before it solidified, the Al‐1%Zn alloy was found to have not only a much higher strain rate at the hot spot of the test bar than that of the Al‐4%Zn alloy, but also a higher strain gradient along the longitudinal direction. In the last six seconds before they solidified, the effective strain at the hot spot for the Al‐1%Zn alloy increased from 0 to 0.021, while the effective strain at the same location increased from 0.075 to 0.20 for the Al‐4%Zn alloy. A strain gradient of 0.0026 mm‐1 against the longitudinal length of the Al‐1%Zn alloy was observed, higher than the 0.0012 mm‐1 of the Al‐4%Zn. It is believed that both the high strain rate and high strain gradient are attributable to the formation of hot tears in the Al‐1%Zn alloy. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary