TEMPO-Oxidized Nanocellulose Films Modified by Tea Saponin Derived from Camellia oleifera: Physicochemical, Mechanical, and Antibacterial Properties

Nan Jiang,Yudi Hu,Yuhang Cheng
DOI: https://doi.org/10.3390/polym16071016
IF: 5
2024-04-09
Polymers
Abstract:Nanocellulose materials have been widely used in biomedicine, food packaging, aerospace, composite material, and other fields. In this work, cellulose obtained from Camellia shells through alkali boiling and subbleaching was micro-dissolved and regenerated using the DMAc (N,N-Dimethylacetamide)/LiCl system, and TOCNs (TEMPO-oxidized cellulose nanofibers) with different degrees of oxidation. The membrane was prepared by filtration of polytetrafluoroethylene (pore size 0.1 μm), and the oxidized nanocellulose film was obtained after drying, Then, the crystallinity, mechanical properties and oxygen barrier properties of the TOCN film were investigated. Furthermore, based on TS (tea saponin) from Camellia oleifera seed cake and TOCNs, TS-TOCN film was prepared by the heterogeneous reaction. The TS-TOCN film not only shows excellent oxygen barrier properties (the oxygen permeability is 2.88 cc·m−2·d−1) but also has good antibacterial effects on both Gram-negative and Gram-positive bacteria. The antibacterial property is comparable to ZnO-TOCN with the same antibacterial content prepared by the in-situ deposition method. Antioxidant activity tests in vitro showed that TS-TOCN had a significant scavenging effect on DPPH (2,2-Diphenyl-1-picrylhydrazyl) radicals. This design strategy makes it possible for inexpensive and abundant Camellia oleifera remainders to be widely used in the field of biobased materials.
polymer science
What problem does this paper attempt to address?
The paper attempts to address the following key issues: 1. **Development of natural antibacterial nanocellulose materials**: With the increasing shortage of non-renewable resources and environmental pollution, there is an urgent need to develop biodegradable natural materials. This study aims to utilize the abundant biomass resource of Camellia oleifera shells to prepare nanocellulose films with excellent performance. 2. **Improvement of the physicochemical properties of nanocellulose films**: By treating nanocellulose with TEMPO oxidation, the carboxyl content is increased, thereby enhancing the mechanical properties and oxygen barrier performance of the films. 3. **Endowing nanocellulose films with antibacterial and antioxidant properties**: By introducing tea saponin (TS), TS-TOCN composite films are prepared, which not only have good oxygen barrier properties but also exhibit antibacterial effects against both Gram-negative and Gram-positive bacteria, as well as significant antioxidant capacity. Specifically, the study achieved these goals through the following steps: - **Raw material processing**: Cellulose is extracted from Camellia oleifera shells, and hemicellulose and lignin are removed through alkaline cooking and sodium hypochlorite bleaching to obtain high-purity cellulose. - **Nanocellulose preparation**: Cellulose is dissolved and regenerated using the DMAc/LiCl system, and then nanocellulose with different degrees of oxidation (TOCNs) is prepared through TEMPO oxidation. - **Film preparation**: Nanocellulose films are prepared by filtering through a polytetrafluoroethylene membrane (pore size 0.1 µm) and drying to obtain TOCN films. - **Tea saponin modification**: The TOCN films are immersed in a tea saponin aqueous solution, and esterification is used to graft tea saponin onto the surface and inside of the films, resulting in TS-TOCN composite films. - **Performance testing**: The prepared films are tested for physicochemical properties, mechanical properties, oxygen barrier performance, antibacterial performance, and antioxidant performance to verify their comprehensive properties. In summary, this study aims to develop a multifunctional natural nanocellulose film through an efficient preparation method to meet the application needs in food packaging and medical fields.