High-capacity full lithium-ion cells based on nanoarchitectured ternary manganese–nickel–cobalt carbonate and its lithiated derivative

J. Q. Zhao,Y. Wang

DOI: https://doi.org/10.1039/c4ta02574a

IF: 11.9

2014-07-10

Journal of Materials Chemistry A

Abstract:A full lithium-ion battery cell has been assembled based on nanoarchitectured ternary manganese–nickel–cobalt compounds, in which multi-shell spherical Mn0.54Ni0.13Co0.13(CO3)0.8 serves as the anode and the subsequently lithiated Li-excess Li[Li0.2Mn0.54Ni0.13Co0.13]O2 with a yolk–shell structure acts as the cathode. The performance of a lithium-ion full battery significantly relies on the electrochemical properties of both anode and cathode materials. A multi-shell carbonate anode is first tested in a half battery cell with metallic lithium as the counter electrode, revealing an unexpectedly high initial charge capacity of 1173.1 mA h g−1 at a specific current of 25 mA g−1, which is two times higher than its theoretical capacity. Moreover, when cycled at 250 mA g−1 for 100 electrochemical cycles, this carbonate anode retains a final specific capacity of 434.6 mA h g−1. Accordingly, a yolk–shell-structured Li-excess layered cathode material has been facilely obtained through lithiation of carbonate compounds, showing an initial discharge capacity of 250.7 mA h g−1 when cycled at 0.1 C (1 C = 250 mA g−1) in a half battery cell. Furthermore, this cathode retains a final capacity of 156.3 mA h g−1 at 1 C after 100 cycles and exhibits an outstanding capacity retention of 90.3%. Such remarkable electrochemical properties of carbonate anode and Li-excess oxide cathode materials are attributed to their nanoarchitectures resulting from the water-based solvothermal process, i.e., multi-shell and yolk–shell structures composed of numerous primary nanoparticles, in comparison with mediocre performances from monodispersive carbonate microspheres and Li-excess oxide nanoparticles synthesized via an ethylene-glycol-based solvothermal method. Combination of the nanostructured ternary transition metal carbonate anode and the Li-excess layered cathode into a full lithium-ion battery results in a remarkable specific capacity above 250 mA h g−1 at 0.1 C in the voltage range of 0.1–4.0 V, which demonstrates the application as a very promising electrochemical device for future energy conversion and storage.

materials science, multidisciplinary,chemistry, physical,energy & fuels