Nickel-rich ternary cathode material as a novel capping layer to improve lithium iron phosphate electrochemical performance

Chengyu Pan,Bowen Li,Haoyan Yin,Xinyue He,Yanmin Gao

DOI: https://doi.org/10.1016/j.electacta.2024.144421

IF: 6.6

2024-05-17

Electrochimica Acta

Abstract:We use a facile high-temperature solid-phase method to coat a layer of Ni-rich ternary material (LiNi 0.8 Co 0.1 Mn 0.1 O 2 ) on the surface of lithium iron phosphate. This active coating greatly improves the intrinsic conductivity of LiFePO 4 . Compared to the conventional carbon material cladding, since this cladding layer is electrochemically active, the problem of decreasing the proportion of active material due to the addition of a cladding layer can be avoided to a certain extent. Compared with the samples capped with conventional organic carbon source (151.2 mAh g −1 ) and inorganic carbon source (155.9 mAh g −1 ) at 0.2C, the discharge specific capacity was as high as 165.7 mAh g −1 . Capacity retention after 200 cycles is up to 98%, which is much higher than that of glucose and graphene oxide (GO)-coated samples (95.9%, 96.6%). Even when charging and discharging cycles are performed at different multipliers (2C and 10C), the retention rate remains higher than the latter.

electrochemistry