Abstract:Adding oxygen into the lead-cooled fast reactor (LFR) to generate a protective oxide layer is one of the most promising methods to mitigate the corrosion of structural materials caused by flowing lead-based coolants such as lead–bismuth eutectic (LBE). In LFRs, the growth-removal behavior of the protective oxide layer is influenced by various factors such as temperature, oxygen concentration, coolant velocity, and etc. Meanwhile, the formation of the oxide layer also changes the thermal–hydraulic characteristics and neutronics parameters of the reactor core. Historically, there has been a lack of research on the coupling effects of neutronics-thermal-hydraulics-materials (N-TH-M) under oxidation-corrosion conditions. In this paper, an N-TH-M multi-physics fields coupling framework was developed to study the key coupling parameters and oxidation corrosion characteristics of an LFR fuel assembly. The results indicate that the formation of the double oxide layer deteriorates the heat transfer between LBE/cladding, which results in the increases of 17.51 K and 10.04 K for maximum temperatures of fuel and cladding under the high oxygen concentration condition. The outer magnetite layer is severely dissolved by flowing LBE, while the inner Fe-Cr spinel layer exhibits good −dissolution resistance. The increase in oxygen concentration can inhibit the dissolution of magnetite and increase the thickness of magnetite, resulting in a 71 % reduction in the average removal thickness and a 5.88 μm increase in the average thickness of the magnetite layer. However, it has no significant effect on Fe-Cr spinel. The rise in coolant inlet temperature has a promoting effect on both the growth and the dissolution of the double oxide layer. With rise of coolant inlet temperature, the growth-promoting effect increases the average thickness of the double oxide layer from 14.11 μm to 27.82 μm. Additionally, the increase in coolant inlet velocity usually has a negative impact on the double oxide layer thickness.

Effect analysis of oxide layer on thermal hydraulic characteristics of LBE cooled reactor

Coupled Analysis of Oxidation Corrosion and Heat Transfer in Lead-Cooled Fast Reactors

Numerical investigation on the Multi-Physics coupling characteristics of Lead-Bismuth reactor fuel assembly based on oxidation corrosion behaviors

Numerical simulation of corrosion phenomena in oxygen-controlled environment for a horizontal Lead-bismuth reactor core

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Long-Term Behaviors of Oxide Layer in Liquid Lead–Bismuth Eutectic (LBE), Part II: Model Applications

Radioactive study of oxidation-corrosion materials activated by neutron in lead-bismuth eutectic reactors

Prediction of Dissolved Impurities and Movement of Oxide Particles in the Primary Circuit of LBE Fast Reactor

Long-Term Behaviors of Oxide Layer in Liquid Lead–Bismuth Eutectic (LBE), Part I: Model Development and Validation

Review of the studies on fundamental issues in LBE corrosion

Improved cellular automata modeling of corrosion/oxidation mechanism of stainless steel in LBE

The study of corrosion characteristics of lead–bismuth eutectic supercritical carbon dioxide microchannel heat exchanger

Corrosion Kinetics and Mechanisms of 15-15Ti Steel in Flowing Liquid Lead-Bismuth Eutectic at 500°C

Corrosion kinetics of T91 steel under low oxygen conditions (10 −7 wt% O) in lead-bismuth eutectic at 500 °C

Modeling of oxidation of structural materials in LBE systems

Study of lead-bismuth eutectic on material performance degradation and life assessment for modified 9Cr-1Mo steel under low cycle fatigue at high temperatures

Corrosion Kinetics of T91 Steel under Low Oxygen Conditions (10-7 Wt% O) in Lead-Bismuth Eutectic at 500 ºc

Corrosion Behavior and Surface Treatment of Cladding Materials Used in High-Temperature Lead-Bismuth Eutectic Alloy: A Review

CFD Analysis of Scaled Wire-wrapped rod Bundle Cooled by LBE

Oxygen Transport Analysis in Lead-Bismuth Eutectic Coolant for Solid-Phase Oxygen Control

Numerical study of solid-state oxygen control bypass performance and corrosion distribution in a LBE flow loop