High-Frequency Surface Insulation Strength with Nanoarchitectonics of Disiloxane Modified Polyimide Films
Zhaoliang Xing,Chong Zhang,Naifan Xue,Zhihui Li,Fei Li,Xiangnan Wan,Shaowei Guo,Jianhong Hao,Zhaoliang Xing,Chong Zhang,Naifan Xue,Zhihui Li,Fei Li,Xiangnan Wan,Shaowei Guo,Jianhong Hao
DOI: https://doi.org/10.3390/polym14010146
IF: 5
2021-12-31
Polymers
Abstract:High-frequency power transformers are conducive to the reliable grid connection of distributed energy sources. Polyimide is often used for the coating insulation of high-frequency power transformers. However, creeping discharge will cause insulation failure, therefore, it is necessary to use disiloxane for the purpose of modifying the molecular structure of polyimide. This paper not only introduces 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (GAPD) with a molar content of 1%, 2%, and 5% to polyimide, but also tests both the physical and chemical properties of the modified film and the high frequency creeping dielectric strength. The results show that after adding GAPD, the overall functional groups of the material do not change, at the same time the transfer complexation of intermolecular charge and the absorption of ultraviolet light increase. There is no phase separation of the material and the structure is more regular and ordered, moreover the crystallinity increases. The overall dielectric constant and the dielectric loss tangent value show different trends, which means that the former value increases, while the latter value decreases. In addition, the resistivity of the surface and the volume increase, which is the same as the glass transition temperature. The mechanical properties are excellent, and the strength of bulk breakdown is mounting. The insulation strength of the high frequency creeping surface has been improved, which will increase with larger contents of GAPD. Among them, the relative change of the creeping flashover voltage is not obvious, and the creeping discharge life of G5 is 4.77 times that of G0. Further analysis shows that the silicon-oxygen chain links of the modified film forms a uniformly dispersed Si-O-Si network in the matrix through chemical bonds and charge transfer complexation. Once the outer matrix is destroyed, it will produce dispersed flocculent inorganic particles which have the role of protecting the inner material and improving the performance of the material. Combined with the ultraviolet light energy absorption, the increase of deep traps, the reduction of dielectric loss, and the improvement of thermodynamic performance, can better improve the high-frequency creeping insulation strength of polyimide film and its potential application value.
polymer science