Study on the Nucleation Mechanism of Carbonitrides on LaAlO 3 in GH4742 superallloy
Shulei Yang,Qiang Tian,Shufeng Yang,Kyung-Woo Yi,Wei Liu,Jingshe Li,Mengjing Zhao
DOI: https://doi.org/10.1016/j.jmrt.2023.08.225
IF: 6.267
2023-08-27
Journal of Materials Research and Technology
Abstract:In this study, focused ion beam (FIB) and transmission electron microscopy (TEM) were used to investigate the morphology, composition, crystal structure, and phase interface growth orientation of the LaAlO 3 -Ti(C,N)-(Ti,Nb,Mo)C complex inclusion in GH4742 alloy. Based on the theory of lattice mismatch and the thermodynamic model of inclusion formation, the formation mechanism of composite inclusions was studied. Crystallographic analysis showed that Ti(C,N) grew on the LaAlO 3 substrate, and its growth was restricted by the parallel orientation relationship with the LaAlO 3 substrate. The (00 06 ̄ )LaAlO 3 //( 1 ̄11 )Ti(C,N) was the lowest lattice mismatch plane between the two phases, with a 1D lattice mismatch of 9.68% and a 2D lattice mismatch of 10.05%. The distance difference between two parallel planes was compensated by dislocations and lattice distortions. Ti(C,N) had lower lattice mismatch with TiC and LaAlO 3 , making it easier to grow on the LaAlO 3 nucleus. Thermodynamic calculations indicate that oxides exist in solid form within the molten alloy. As the temperature decreases, TiN precipitates in the alloy melt, while TiC precipitates during the solidification process. These results provide an explanation for the formation process of the complex three-layer structure of the complex inclusions.
materials science, multidisciplinary,metallurgy & metallurgical engineering