Preparation of flame retardant and conductive epoxy resin composites by incorporating functionalized multi‐walled carbon nanotubes and graphite sheets

Sheng Zhang,Yichong Jiang,Yongyuan Sun,Jun Sun,Bo Xu,Hongfei Li,Xiaoyu Gu

DOI: https://doi.org/10.1002/pat.5239

IF: 3.348

2021-02-07

Polymers for Advanced Technologies

Abstract:<p>This work reports our recent efforts on the preparation of functionalized multi‐walled carbon nanotubes (f‐CNTs) and its application in improving the fire, conductive, and mechanical performance of epoxy resin (EP) composites in combination with graphite sheets (GSs). The addition of hybrid carbon nanomaterials can effectively improve the mechanical properties of epoxy. Consequently, when the mass fraction of f‐CNTs/GSs is 3.9 wt%, the limiting oxygen index (LOI) value is increased to 27.4%, and the tensile strength and notched impact strength of epoxy are increased by 33.5% and 44.8%, respectively. Increasing the content of carbon nanomaterials can further improve the flame retardancy and electrical conductivity of EP composites. For the sample containing 11.0 wt% f‐CNTs/GSs, the electrical conductivity is further increased to 1.7 × 10⁻³ S/cm, which can be regarded as conductive materials. The LOI value is reached to 28.6%, with peak heat release and total heat release reduced by 26.4% and 16.4%, respectively.</p>

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to prepare epoxy resin composites with enhanced flame retardancy, electrical conductivity and mechanical properties by adding functionalized multi - walled carbon nanotubes (f - CNTs) and graphite sheets (GSs). Specifically, the research aims to explore the dispersibility of these nanomaterials in epoxy resin and their influence on the flame retardancy, electrical conductivity and mechanical properties of epoxy resin composites, in order to develop high - performance flame - retardant and antistatic polymer composites to meet the growing market demand.

The paper mentions that although the original epoxy resin (EP) is widely used in high - tech fields such as integrated circuits and composites due to its excellent adhesiveness, high mechanical strength, high thermal stability, low dielectric constant and loss, easy processability and good dimensional stability, it has defects such as flammability, poor toughness and easy static electricity accumulation. Therefore, how to prepare high - performance flame - retardant and antistatic polymer composites has become a hot issue in academia and industry.

In order to improve these problems, the author adopted a method of combining multi - walled carbon nanotubes (f - CNTs) modified by 3 - glycidoxypropyltrimethoxysilane (GPTES) with graphite sheets (GSs), and prepared epoxy resin composites through a simple process flow, and carried out detailed characterization and performance tests on them. The results show that when the mass fraction of f - CNTs/GSs is 3.9 wt%, the limiting oxygen index (LOI) value of epoxy resin increases to 27.4%, and the tensile strength and notched impact strength are increased by 33.5% and 44.8% respectively. With the increase of the content of carbon nanomaterials, the flame retardancy and electrical conductivity of epoxy resin composites are further improved. When the mass fraction of f - CNTs/GSs reaches 11.0 wt%, the electrical conductivity is increased to 1.7 × 10\(^{-3}\) S/cm, the LOI value reaches 28.6%, and at the same time, the peak heat release rate and the total heat release rate are reduced by 26.4% and 16.4% respectively.

In conclusion, this research has successfully significantly improved the flame retardancy, electrical conductivity and mechanical properties of epoxy resin composites by adding f - CNTs and GSs, providing the possibility for the industrial application of high - performance flame - retardant and antistatic polymer composites.