Abstract:<p>Rotary ultrasonic machining (RUM) has been considered as an effective approach in the manufacturing of advanced materials such as ceramic matrix composite (CMC). However, the distinct removal mechanisms in RUM with different vibration forms has not been elucidated, which hinders the adoption of RUM technology in the field of material processing. In this research, the ultrasonic-assisted scratching tests of CMC were conducted to reveal the fundamentals of material removal and surface formation. Based on the kinematics of RUM processes, the vibration effects exerted in cutting areas were clarified as impact-separation and reciprocating-polishing, thus two types of diamond indenters have been specially designed for the intermittent and continuous scratching tests, respectively. The scratching force, friction factor and grooves morphology have been analyzed and compared with that of the conventional scratching without vibration. For the intermittent scratching with vertical vibration, it was found that the high frequency impact-separation between indenter and workpiece increased the critical penetration depth of ductile-brittle transition, which can help restrain the cracking defects of CMC. For the continuous scratching with tangential vibration, the overlapping rate was firstly proposed to evaluate the effect of reciprocating polishing. It was shown that higher overlapping rate and larger dynamic shear angle can be achieved by matching the scratching velocity with vibration frequency, which is conducive to obtaining even fiber fracture and better surface integrity. Due to the minimal volume of material removed in each vibration cycle, the scratching resistance was significantly lowered with smaller fluctuation under both vibration forms. Moreover, the diminishing of vibration effectiveness at certain scratching parameters was also discussed. This research work brings in a better understanding on the material removal mechanisms under different effects of ultrasonic vibration, which can provide a guidance for the design and optimization of the vibration assisted processing of advanced materials.</p>

Vibration-assisted material damage mechanism: From indentation cracks to scratch cracks

Study on Mechanism for Material Removal and Surface Generation by Molecular Dynamics Simulation in Abrasive Processes

Interference mechanism and damage accumulation in high-speed cross scratches on hard brittle materials

Theoretical modeling and experimental analysis of single-grain scratching mechanism of fused quartz glass

Crack extension mechanism and scratch stress field model of hard and brittle materials caused by curvature effect

High-frequency vibration effects on material removal mechanisms in ultrasonic transverse scratching of carbon fiber reinforced plastics

Material removal and damage formation mechanisms induced by periodic indentation during ultrasonic vibration-assisted scratching of SiC f /SiC composites

Cracking behavior during scratching brittle materials with different-shaped indenters

Insights into scratching force in axial ultrasonic vibration-assisted single grain scratching

Study of the inhibition mechanism of sapphire subsurface damage by tangential ultrasonic vibration

Mechanical response of single-crystal copper under vibration excitation based on molecular dynamics simulation

Study on the surface formation mechanism in scratching test with different ultrasonic vibration forms

Curvature effect induced cutting stress field offset and its influence on the damage of hard and brittle materials

Coupling of double grains enforces the grinding process in vibration-assisted scratch: Insights from molecular dynamics

Subsurface damage evaluation in the single abrasive scratching of BK7 glass by considering coupling effect of strain rate and temperature

Damage and removal behaviors of indium phosphide crystals involved in ultrasonic vibration-assisted AFM machining

Scratch-induced micro-fracture behaviour and translational failure of glass: An experimental and numerical study

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Optimization of grinding process for hard and brittle materials based on damage evolution mechanism

Cross-point effect of high-speed cross scratch on hard brittle materials

Study on the Vertical Ultrasonic Vibration-Assisted Nanomachining Process on Single-Crystal Silicon