Abstract:Siliceous mesostructured cellular foams (MCF) impregnated with polyethylenimine (PEI) of various molecular weights and structures were evaluated as CO2 adsorbents. The MCF solid support consisted of a well-defined interconnected three-dimensional mesoporous structure with large cell diameter of 30.3 nm and large window diameter of 11.3 nm, filled with polyethylenimine up to 70 weight percent or about 22.3% nitrogen atom by weight of the adsorbents. While other mesoporous solid supports lost their porosity after PEI impregnation, our MCF solid support maintained its pore volume over the range of 1.12 to 1.64 cm(3) g(-1). The importance of the porosity of PEI-impregnated MCF adsorbents for high capacity CO2 adsorbents was demonstrated. The highest CO2 sorption capacity (180.6 mg-CO2/g-adsorbent or 393.6 mg-CO2/g-PEI at 75 degrees C) was obtained for silica supports loaded with 50 weight percent branched PEI with average molecular weight of 600 g mol(-1). Under dry atmospheric CO2 gas, this adsorbent reached the theoretical CO2 capacity of 0.50 mole-CO2 per mole-nitrogen within less than about 8 min, making this adsorbent one of the most effective CO2 adsorbents reported. Repeated multiple sorption cycles demonstrated good stability of this adsorbent for CO2 capture. The initial sorption kinetics determined the overall CO2 sorption capacity, which was limited by the formation of a carbamate layer as a result of the CO2-PEI complexation that due to inhibition of CO2 diffusion; the kinetics of "ionic" gelation of the impregnated PEI by CO2 controlled the overall performance of the CO2 adsorbents. At 75 degrees C, the operating temperature favored the molecular mobility of PEI and unrestricted diffusion of CO2 to allow the theoretical CO2 capacity of the PEI to be attained. Lower temperatures limited the mobilities of PEI and CO2 and the kinetics of "ionic" gel formation dominated, causing a lowered overall performance of the CO2 adsorbents. Overall, this study points to the importance of interconnected porous channel networks to optimize the performance of PEI-impregnated mesoporous silica particles.

Sponge-like polyethyleneimine adsorbents with interconnected open channels enabling ultra-high CO 2 adsorption and separation capacity

Polyethylenimine-Grafted Hkust-Type Mof/Poiyhipe Porous Composites (Pei@Pgd-H) As Highly Efficient Co(2 )Adsorbents

Polyethyleneimine-Modified UiO-66-NH2(Zr) Metal–Organic Frameworks: Preparation and Enhanced CO2 Selective Adsorption

A stable solid amine adsorbent with interconnected open-cell structure for rapid CO2 adsorption and CO2/CH4 separation

Preparation of porous CO 2 adsorbent with high amine-content matrix by unique emulsion template

Polyethylenimine-impregnated resin for high CO2 adsorption: an efficient adsorbent for CO2 capture from simulated flue gas and ambient air.

Polyethylenimine-Impregnated Siliceous Mesocellular Foam Particles As High Capacity Co2 Adsorbents

Preparation of a laminated structured polyethyleneimine cryogel for carbon capture

Physicochemical synergistic adsorption of CO2 by PEI‐impregnated hierarchical porous polymers

Polyethyleneimine-Nano Silica Composites: A Low-Cost And Promising Adsorbent For Co2 Capture

Control of Uniform and Interconnected Macroporous Structure in PolyHIPE for Enhanced CO2 Adsorption/Desorption Kinetics.

Crosslinked polyethyleneimine‐based structures in different morphologies as promising CO2 adsorption systems: A comprehensive study

Tuning the Acidity and Textural Properties for Enhanced Economical CO2 Capture in Polyethyleneimine (PEI) Supported Adsorbents

Enhanced Adsorption of Carbon Dioxide from Simulated Biogas on PEI/MEA-Functionalized Silica

Adsorptive Removal of Carbon Dioxide Using Polyethyleneimine Supported on Propanesulfonic-Acid-Functionalized Mesoporous SBA-15

Effective adsorption of Ultra-dilute CO2 over Polyethyleneimine-based adsorbent for H2 purification

Enhanced selective adsorption of H 2 S from CO 2 by incorporating methylated polyethyleneimine into a porous carbon matrix

Development of amine-pillar[5]arene modified porous silica for CO2 adsorption, and CO2/CH4, CO2/N2 separation

Polyethyleneimine-modified layered double hydroxide/SBA-15 composites: A novel kind of highly efficient CO2 adsorbents

Amine-impregnated natural inorganic nanotubes via layer-by-layer electrostatically self-assembly approach for efficient CO 2 adsorption

Experimental testing and mechanism investigation of amine-functionalized layered vermiculite for CO 2 capture