Abstract:To explore room-temperature strengthening and high-temperature ductility, a lightweight novel Mg-1.85Gd-0.64Al-0.62Zn alloy was fabricated by innovative multidirectional forging and a hot-rolling technique. Microstructures and mechanical properties were studied at room and elevated temperatures with an optical microscope, an X-ray diffractometer, and a tensile tester. An ultimate tensile strength of 260 MPa, yield strength of 171 MPa, and elongation of 20.4% were demonstrated at room temperature. The room-temperature strengthening mechanisms were identified by strengthening the model estimation. A type C Portevin-Le Chatelier effect was discovered and elucidated in this alloy. X-ray diffraction analysis revealed that the phase composition is α-Mg solid solution and (Mg, Al)3Gd, Al7Zn3, and Al2Gd intermetallic compounds. Examination of the microstructure at elevated temperatures revealed that dynamic recrystallization and dynamic grain growth occur. In particular, it was discovered that bimodal microstructures or incomplete dynamic recrystallization microstructures exist in high-temperature deformation. A maximum quasi-superplasticity of 228.4% was demonstrated in this alloy at 673 K and 5.0 × 10-4 s-1. Flow stress curves showed that the present alloy exhibits Sotoudeh-Bate curves or a long intermediate strain-hardening stage followed by a strain-softening stage. A modified Zerilli-Armstrong constitutive equation incorporating the number of dislocations was established. The power-law constitutive equation was established to identify the deformation mechanism. Both constitutive models had good predictability. At 673 K and 5.0 × 10-4 s-1, the stress exponent was 4, and the average deformation activation energy was 104.42 kJ/mol. The number of dislocations inside a grain was 146. This characteristic evidence confirmed that dislocation motion controlled by pipe diffusion dominates the rate-controlling process under this condition.

Unexpected high-temperature brittleness of a Mg-Gd-Y-Ag alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

The high-temperature deformation and microstructural evolution mechanism of Mg-Gd-Y-Zn-Zr alloy formed by CMT arc additive forming

Deformation modes and fracture behaviors of peak-aged Mg-Gd-Y alloys with different grain structures

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Flow softening and dynamic recrystallization behavior of a Mg-Gd-Y-Nd-Zr alloy under elevated temperature compressions

Hot Deformation Behavior and Processing Map of Coarse-Grained Mg–Gd–Y–Nd–Zr Alloy

The abnormal flow behavior of Mg-9Gd-4Y-2Zn-0.5Zr alloy during hot tensile deformation at high temperature and low strain rate

Hot Deformation Behaviour and Constitutive Equation of Mg-9Gd-4Y-2Zn-0.5Zr Alloy

Room-Temperature Strengthening, Portevin-Le Chatelier Effect, High-Temperature Tensile Deformation Behavior, and Constitutive Modeling in a Lightweight Mg-Gd-Al-Zn Alloy

Research on microstructure and mechanical properties of hot extruded Mg-Gd-Y-Sm-Zr alloy at room and high temperatures

Hot compression behavior and microstructure evolution of Mg-Gd-Y-Zn-Zr alloy

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

Clarifying the deformation modes and strengthening mechanisms of Mg-11Gd-5Y-2Zn-0.7Zr with outstanding high-temperature mechanical properties

Effect of Ag Addition on the Hot Deformation, Constitutive Equations and Processing Maps of a Hot Extruded Mg-Gd-Y Alloy

Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures

High temperature deformation behavior of Mg-5wt.%Y binary alloy: Constitutive analysis and processing maps