Abstract:Study on the corrosion behavior of reinforcing steel is one of the most significant research topics in the field of corrosion and protection of metals. The scanning microelectrode technique is a powerful tool to study localized corrosion behavior of reinforcing steel in a corrosive solution. In this work, the corrosion behavior of reinforcing steel in a simulated concrete pore solution with Cl - and the inhibition effect of a mixture of NaNO 2 and Na 2 SiO 3 on the steel were studied by the scanning microelectrode technique assisted by polarization curve measurements and surface analyses. Q235 reinforcing steel was used as the tested material. The cylindrical steel specimen with dimension of Æ1.14 cm ´ 0.50 cm was sealed in a PVC holder enveloped with epoxy resin, and only a cross section (1.00 cm 2 ) of the steel served as the working surface. Before experiments, the steel specimen was sequentially polished by silicon carbide sandpaper up to 1500 grit and 0.3 µm Al 2 O 3 powder, and then ultrasonically cleaned in deionized water and ethanol. A saturated Ca(OH) 2 solution was used as the simulated concrete pore (SCP) solution. The simulated polluted concrete pore (SPCP) solution was prepared from SCP solution by adjusting its pH to 11.50 with deionized water and adding 0.05 M NaCl. NaNO 2 and Na 2 SiO 3 with different concentrations as corrosion inhibitors were added to the SPCP solution. The potential distribution on the reinforcing steel surface was measured by a home-built scanning microelectrode measurement system. Ag/AgCl electrodes were used as a scanning microprobe and a micro-reference electrode. Polarization curve measurements were carried out by an Autolab Potentiostat Galvanostat. A three–electrode cell was used with the steel specimen as the working electrode, a saturated calomel electrode (SCE) as the reference electrode and a platinum electrode as the counter electrode. All the measurements were performed at ambient temperature. The results showed that there were no stable large potential peaks on the steel surface in the pure Ca(OH) 2 solution with pH 12.50 or 11.50, indicating that the steel surface was in a passive state and no corrosion took place. For the steel in the SPCP solution with 0.050 M NaCl and pH 11.50, a stable and large local potential peak occurred on its potential map after 20 min immersion. This result indicated that the steel was active and localized corrosion occurred resulting from the Cl - attack. For the SPCP solution with 0.004 M NaNO 2 and 0.001 M Na 2 SiO 3 , there were no stable potential peaks on the potential map of the steel immersed in the solution for 8 h, indicating that no localized corrosion took place. Therefore, the mixture of NaNO 2 with Na 2 SiO could protect the reinforcing steel from corrosion. The polarization curve measurements and surface analyses also confirmed the above results. This work was supported by the National Natural Science Foundation of China (Nos. 21073151, and 21173177).

Corrosion Protection of Steel by NO3− and NO2− Intercalated Mg-Al Layered Double Hydroxides in Simulated Pore Solutions of Alkali-Activated Slag

A Composite Corrosion Inhibitor of MgAl Layered Double Hydroxides Co-Intercalated with Hydroxide and Organic Anions for Carbon Steel in Simulated Carbonated Concrete Pore Solutions

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Study on Synergistic Corrosion Inhibition Effect between Calcium Lignosulfonate (CLS) and Inorganic Inhibitors on Q235 Carbon Steel in Alkaline Environment with Cl−

Enhanced corrosion resistance and applicability of Mg/Al-CO<sub>3</sub><SUP>2-</SUP> layered double hydroxide film on Q235 steel substrate

The Combined Effect of Carbonation and Chloride-Contamination of Concrete on the Intelligence of Mg Alloy Sacrificial Anode for Reinforcing Steel

Effect of LDHs-ALA on Steel Corrosion in Chloride-Rich Simulated Concrete Pore Solution: Experimental and DFT Studies

Influence of MgAl-NO2-LDHs on Passivation of Reinforcing Steel in Simulated Geopolymer Solution

Potential Utilization of Sludge Extract As Corrosion Inhibitor for Reinforcing Steel in Alkaline Environment

A Combined Inhibiting Effect of Sodium Alginate and Sodium Phosphate on the Corrosion of Magnesium Alloy Az31 in Nacl Solution

Beneficial and Detrimental Impacts of Molybdate on Corrosion Resistance of Steels in Alkaline Concrete Pore Solution with High Chloride Contamination

Corrosion Inhibition Effect of Mg-Al-pAB-LDH Coating for Steel in the Marine Environment

Inhibiting property of nitrite intercalated layered double hydroxide for steel reinforcement in contaminated concrete condition

Multifunctional Corrosion Inhibition Behavior of Zn-Al Calcined Layered Double Hydroxides for Steel Rebar in NaCl Solution

The Influence of Chlorides on Corrosion Behavior of Carbon Steel in Slag Based Geopolymer Pore Solution

Electrochemical Performance of Low-Alloy Steel and Low-Carbon Steel Immersed in the Simulated Pore Solutions of Alkali-Activated Slag/steel Slag Pastes in the Presence of Chlorides

Study on Corrosion Inhibition of Reinforcing Steel in Simulated Concrete Pore Solutions by Scanning Microelectrode Technique

Passive Behaviour of New Alloy Corrosion Resistant Steel Cr10Mo1 in Simulating Concrete Pore Solutions with Different Chloride Contents

Inhibitive Effect of Sodium Molybdate on the Corrosion Behavior of Galvanized Steel in Simulated Concrete Pore Solution

Passive Behavior of New Alloy Corrosion Resistant Steel Cr10Mo1 in Chloride-containing Environment

Corrosion Behavior of Zn-Al, Zn-Mg, and Zn-Mg-Al Coatings in Simulated Concrete Pore Solution